Preparation and properties of polypyrrole/silver conductive polyester fabrics

LIN Jiameng, WAN Ailan, MIAO Xuhong()   

  1. Engineering Research Center for Knitting Technology, Ministry of Education, Jiangnan University, Wuxi, Jiangsu 214122, China
  • Received:2019-03-01 Revised:2019-11-07 Online:2020-03-15 Published:2020-03-27
  • Contact: MIAO Xuhong

摘要:

为拓展聚吡咯/银(PPy/Ag)导电涤纶织物的应用领域,在等离子体预处理涤纶织物的条件下,以硝酸银为氧化剂,采用一锅法制备PPy/Ag导电涤纶织物。借助傅里叶红外光谱仪、X 射线衍射仪和扫描电子显微镜等对导电织物进行表征,通过电阻仪测试导电织物的方阻值,采用琼脂平皿法测试其抑菌效果。结果表明:制备的PPy/Ag导电涤纶织物具有良好的导电性,并对大肠杆菌和金黄色葡萄球菌具有明显的抑制作用;导电织物的导电性与等离子体预处理涤纶织物的次数呈正相关,且在等离子体预处理4次时,其方阻达到最小值0.22 kΩ/□。

关键词: 导电织物, 聚吡咯, 纳米银, 等离子体预处理, 涤纶, 导电性, 抗菌性

Abstract:

In order to expand the application of polypyrrole/silver (PPy/Ag) conductive polyester fabrics, PPy/Ag conductive polyester fabrics were prepared by one-pot method with silver nitrate as oxidant under the condition of plasma pretreatment. The conductive fabrics were characterized by Fourier transform infrared spectroscopy, X-ray diffraction and scanning electron microscopy. The square resistance of conductive fabrics was measured by resistometer and the bacteriostatic effect was tested by agar plate method. The results show that the PPy/Ag conductive polyester fabrics prepared in this study have good conductivity, and have obvious inhibitory effect on Escherichia coli and Staphylococcus aureus. The conductivity of such fabrics is positively correlated with the number of times of plasma pretreatment to polyester fabrics, and the square resistance of conductive fabrics reaches the minimum value of 0.22 kΩ/□ when the number of plasma pretreatment is 4.

Key words: conductive fabric, polypyrrole, silver nanoparticles, plasma pretreatment, polyester, conductivity, antimicrobial property

中图分类号: 

  • TS195.2

表1

试样及其处理条件"

试样编号 处理条件
0# 未处理的涤纶织物
0-1# 等离子体预处理
1# 吡咯氧化聚合+Ag+还原
2# 等离子体处理2次+吡咯氧化聚合+Ag+还原
3# 等离子体处理3次+吡咯氧化聚合+Ag+还原
4# 等离子体处理4次+吡咯氧化聚合+Ag+还原
5# 等离子体处理5次+吡咯氧化聚合+Ag+还原

表2

试样方阻值及CV值"

试样编号 方阻/(kΩ·□-1) CV值/%
1# 3.94 10.3
2# 1.98 3.9
3# 1.08 2.7
4# 0.22 3.1
5# 0.24 3.7

图1

试样的扫描电镜照片(×5 000)"

图2

试样的红外光谱图 注:PPy为聚吡咯粉末。"

图3

试样的 X 射线衍射光谱"

表3

试样抑菌效果评价"

试样
编号
试样下面细菌
繁殖情况
抑菌带宽度/mm 评价
大肠杆菌 金黄色葡萄球菌
0# 大量 0 0 没有效果
1# 轻微 >1 >1 效果较好
2# 轻微 >1 >1 效果较好
3# 轻微 >1 >1 效果较好
4# 轻微 >1 >1 效果较好
5# 轻微 >1 >1 效果较好

图4

抑菌性能测试结果"

[1] SAHA S, SARKAR J, ACHARYA Y, et al. Production of silver nanoparticles by a phytopathogenic fungus bipolaris nodulosa and its antimicrobial activity[J]. Digest Journal of Nanomaterials & Biostructures, 2010,5(4):887-895.
[2] AJAY SINGH, ZAKARIA SALMI, NIRAV JOSHI, et al. Photo-induced synjournal of polypyrrole-silver nanocomposite films on N-(3-trimethoxysilylpropyl) pyrrole-modified biaxially oriented polyethylene flexible substrates[J]. RSC Advances, 2013,16(3):6-23.
[3] SUN J, YAO L, GAO Z, et al. Surface modification of PET films by atmospheric pressure plasma-induced acrylic acid inverse emulsion graft[J]. Surface and Coatings Technology, 2010,204(24):4101-4106.
[4] KELLER M, RITTER A, REIMANN P, et al. Comparative study of plasma-induced and wet-chemical cleaning of synthetic fibers[J]. Surface and Coatings Technology, 2005,200(4):1045-1050
[5] MEHMOOD T, KAYNAK A, DAI X J, et al. Study of oxygen plasma pre-treatment of polyester fabric for improved polypyrrole adhesion[J]. Materials Chemistry and Physics, 2014,143(2):668-675.
[6] ATTIA M F, AZIB T, SALMI Z, et al. One-step UV-induced modification of cellulose fabrics by polypyrrole/silver nanocomposite films[J]. Journal of Colloid & Interface Science, 2013,393(1):130-137.
[7] JLASSI K, SINGH A, ASWAL D K, et al. Novel, ternary clay/polypyrrole/silver hybrid materials through in situ photopolymerization[J]. Colloid Surf A: Physicochem Eng Asp, 2013,439(Special SI):193-199.
[8] GASHTI M P, GHEHI S T, AREKHLOO S V, et al. Electromagnetic shielding response of UV-induced polypyrrole/silver coated wool[J]. Fibers and Polymers, 2015,16(3):585-592.
[9] 董猛, 田俊莹. 聚吡咯/银导电涤纶织物的开发[J]. 印染, 2015(22):1-4.
DONG Meng, TIAN Junying. Development of polypyrrole/silver conductive polyester fabric[J]. China Dyeing & Finishing, 2015 (22):1-4.
[10] BABU K F, DHANDAPANI P, MARUTHAMUTHU S, et al. One pot synjournal of polypyrrole silver nanocomposite on cotton fabrics for multifunctional property[J]. Carbohydrate Polymers, 2012,90(4):1557-1563.
pmid: 22944416
[11] 张江茹. 聚吡咯基纳米复合粒子的合成、表征及应用研究[D]. 北京:北京化工大学, 2012: 1-16.
ZHANG Jiangru. Study on synthesis,characterization and application of polypyrrole-based nanocomposite particles[D]. Beijing:Beijing University of Chemical Technology, 2012: 1-16.
[1] 于佳, 辛斌杰, 卓婷婷, 周曦. 高导电性铜/聚吡咯涂层羊毛织物的制备与表征[J]. 纺织学报, 2021, 42(01): 112-117.
[2] 邵景峰, 李宁, 蔡再生. 基于模糊多准则的涤纶低弹丝生产工艺参数优化[J]. 纺织学报, 2021, 42(01): 46-52.
[3] 黎俊妤 蒋培清 张文奇 李文斌. 原子层沉积技术对纤维素膜功能化的影响[J]. 纺织学报, 2020, 41(12): 26-30.
[4] 马跃, 郭静, 殷聚辉, 赵秒, 宫玉梅. 纤维素/氧化纤维素/南极磷虾蛋白复合抗菌纤维的制备与表征[J]. 纺织学报, 2020, 41(11): 34-40.
[5] 姜兴茂, 刘奇, 郭琳. 二氧化硅包覆银铜纳米颗粒的结构及其抗菌性能[J]. 纺织学报, 2020, 41(11): 102-108.
[6] 张艳艳, 詹璐瑶, 王培, 耿俊昭, 付飞亚, 刘向东. 用无机纳米粒子制备耐久性抗菌棉织物的研究进展[J]. 纺织学报, 2020, 41(11): 174-180.
[7] 王秋萍, 张瑞萍, 李成红, 张葛成. 导电涤纶非织造布的制备及其性能[J]. 纺织学报, 2020, 41(10): 116-121.
[8] 王博, 凡力华, 原韵, 殷允杰, 王潮霞. 可拉伸聚吡咯/棉针织物的制备及其储电性能[J]. 纺织学报, 2020, 41(10): 101-106.
[9] 李亮, 刘静芳, 胡泽栋, 耿长军, 刘让同. 涤纶织物的氧化石墨烯负载及其抗静电性能[J]. 纺织学报, 2020, 41(09): 102-107.
[10] 秦益民. 含银海藻酸盐医用敷料的临床应用[J]. 纺织学报, 2020, 41(09): 183-190.
[11] 庞雅莉, 孟佳意, 李昕, 张群, 陈彦锟. 石墨烯纤维的湿法纺丝制备及其性能[J]. 纺织学报, 2020, 41(09): 1-7.
[12] 唐峰, 余厚咏, 周颖, 李营战, 姚菊明, 王闯, 金万慧. 聚(3-羟基丁酸-co-3-羟基戊酸共聚酯)复合膜的制备及其性能[J]. 纺织学报, 2020, 41(09): 8-15.
[13] 贾琳, 王西贤, 陶文娟, 张海霞, 覃小红. 聚丙烯腈抗菌复合纳米纤维膜的制备及其抗菌性能[J]. 纺织学报, 2020, 41(06): 14-20.
[14] 王婷婷, 刘梁, 曹秀明, 王清清. 竹红菌素-聚( 甲基丙烯酸甲酯-co-甲基丙烯酸)纳米纤维的制备及其光敏抗菌性能[J]. 纺织学报, 2020, 41(05): 1-7.
[15] 周青青, 陈嘉毅, 祁珍明, 陈为健, 邵建中. 阻燃抗菌棉织物的制备及其性能表征[J]. 纺织学报, 2020, 41(05): 112-120.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!