丝素纳米纤维支架的修饰及其血液相容性

纺织学报 ›› 2011, Vol. 32 ›› Issue (3): 10-14.

丝素纳米纤维支架的修饰及其血液相容性

王曙东^1,2 ; 张幼珠²; 刘华¹;王红卫²; 董智慧³

1. 盐城纺织职业技术学院纺织工程系2. 苏州大学纺织与服装工程学院 3. 复旦大学附属中山医院

收稿日期:2010-04-20 修回日期:2010-08-20 出版日期:2011-03-15 发布日期:2011-03-15
通讯作者: 王曙东

Modification of silk fibroin nanofibrous scaffold and its blood compatibility

WANG Shudong^1,2; ZHANG Youzhu²; LIU Hua¹ ; WANG Hongwei²; DONG Zhihui³

1．Department of Textile Engineering，Yancheng Vocational Technology College 2．College of Textile and Clothing Engineering，Soochow University 3．Zhongshan Hospital, Fudan University

Received:2010-04-20 Revised:2010-08-20 Online:2011-03-15 Published:2011-03-15

摘要/Abstract

摘要：

采用等离子体处理接枝和共混纺丝2种方法将肝素修饰到静电纺丝素纳米纤维支架上，通过扫描电镜和X射线光电子能谱测定和表征修饰效果，并对修饰前后丝素纳米纤维支架进行血小板粘附实验和体外抗凝血实验。结果表明：通过等离子体处理接枝和共混纺丝2种方法均可较好的将肝素修饰到丝素纳米纤维支架上；经肝素修饰后的丝素纳米纤维支架的凝血活酶时间、凝血酶原时间和凝血酶时间显著高于纯丝素纳米纤维支架；未经修饰的纤维支架上出现血小板黏附、凝聚现象，而经肝素修饰后的丝素纤维支架上未出现上述现象。

Abstract:

The electrospun silk fibroin nanofibrous scaffolds were modified with heparin by grafting after plasma treatment and blending electrospinning. The effect of the modification was evaluated by means of SEM and XPS. Platelet adhesion tests and in vitro coagulative time tests were carried out on the silk fibroin nanofibrous scaffolds before and after modification. The results showed that the heparin was successfully introduced to the silk fibroin nanofibrous scaffolds by both two kinds of modification. In vitro coagulative time tests showed that the APTT, PT and TT of the heparin-modified scaffolds were significantly higher than that of the pure silk fibroin scaffolds. Platelet adhesion and aggregation was found on the pure silk fibroin scaffolds. However, it could not be seen on the heparin-modified scaffolds.

王曙东;;张幼珠;刘华;王红卫;董智慧. 丝素纳米纤维支架的修饰及其血液相容性[J]. 纺织学报, 2011, 32(3): 10-14.

WANG Shudong;;ZHANG Youzhu;LIU Hua;WANG Hongwei;DONG Zhihui. Modification of silk fibroin nanofibrous scaffold and its blood compatibility[J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(3): 10-14.