醇处理对静电纺MWNTs/丝素/聚酰胺复合纤维的影响

徐安长,张露,潘志娟   

  1. 苏州大学纺织与服装工程学院
  • 收稿日期:2009-06-03 修回日期:2010-03-04 出版日期:2010-07-15 发布日期:2010-07-15
  • 通讯作者: 潘志娟

Effect of ethanol vapor treatment on properties of electrospun MWNTs/silk fibroin/polyamine 6/66 fibers

XU Anchang;ZHANG Lu;PAN Zhijuan

  

  1. College of Textile and Clothing Engineering, Soochow University
  • Received:2009-06-03 Revised:2010-03-04 Online:2010-07-15 Published:2010-07-15
  • Contact: PAN Zhi-Juan

摘要:

醇蒸汽对改善静电纺纤维的结构与性能具有重要作用。采用静电纺丝的方法制备了MWNTs/丝素/聚酰胺6/66复合纤维毡,并用无水乙醇蒸汽对其处理。研究发现,碳纳米管质量分数较少的试样中,纤维发生了溶胀,并粘连在一起,随着碳纳米管质量分数的增加,纤维只是发生了径向膨胀。乙醇蒸汽处理使纤维毡的结晶结构、热稳定性以及力学性能都得到了显著的提高。碳纳米管质量分数为0.1%时,结晶度从55.8%增加到63.9%,断裂强度、初始模量以及断裂伸长分别增加了45%、103%和134%。

Abstract:

Alcohol vapor treatment is a useful way in improving the structure and properties of electrospun nanofibers. Electrospinning was employed to produce MWNTs/silk fibroin/polyamine 6/66 composite nanofiber mat which was then treated by ethanol vapor. The results indicated that the samples with less mass fraction of MWNTs exhibited swelling and conglutintion, and the fiber with greater mass fraction presented only radial expansion. The ethanol vapor treatment evidently improved the degree of crystallinity, thermal stability and mechanical properties of the electrospun nanofiber mats. After alcohol vapor treatment, the degree of crystallinity of the sample increased from 55.8% to 63.9%, and the breaking strength, initial modulus and breaking elongation increased by 45%, 103% and 134% respectively when the MWNTs mass fraction was 0.1%.

中图分类号: 

  • TS102.6
[1] 许永杉 吴敏 葛明桥. 壳聚糖接枝聚合物的制备及其在聚丙烯非织造布上的应用[J]. 纺织学报, 2015, 36(09): 70-74.
[2] 周月红 沈勇 魏作红 李勇. 超细异形腈纶的结构及其理化性能[J]. 纺织学报, 2015, 36(05): 7-12.
[3] 崔国艳 颜娜 韩冰. 聚乳酸∕聚乙醇酸新型纳米支架载药体系研制[J]. 纺织学报, 2014, 35(12): 6-0.
[4] 季涛, 李杰, 高强, 余进, 刘其霞. 粘胶基炭化织物的制备及工艺优化[J]. 纺织学报, 2012, 33(4): 49-54.
[5] 王春莹;王潮霞. 常压介质阻挡放电对涤纶春亚纺织物的表面改性[J]. 纺织学报, 2010, 31(7): 97-101.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!