纺织学报 ›› 2013, Vol. 34 ›› Issue (4): 12-16.

• 纤维材料 • 上一篇    下一篇

光谱指纹纤维的防伪特性

张技术 葛明桥   

  1. 生态纺织教育部重点实验室(江南大学)
  • 收稿日期:2012-02-20 修回日期:2012-05-31 出版日期:2013-04-15 发布日期:2013-04-09
  • 通讯作者: 葛明桥 E-mail:gemq57@163.com
  • 基金资助:

    教育部科学技术研究重大项目

Anti-counterfeiting characteristics of spectrum-fingerprint fiber

  • Received:2012-02-20 Revised:2012-05-31 Online:2013-04-15 Published:2013-04-09
  • Supported by:

    Key (Key grant) Project of Chinese Ministry of Education

摘要: 为促进光谱指纹防伪纤维的应用推广,本文制备9种纤维样品,借助荧光分光光度计对其防伪特性进行了研究。结果表明:在特定的激发光下,不同原料配方和纺丝工艺参数下纺制的光谱指纹纤维具有的发光谱线类似人的指纹,具有唯一性;经重复测量,该发光谱线具有很好的再现性;存放6个月,水洗2h,或光照5h、或经120℃高温处理2h、或2min酸碱处理后,该发光谱线没有发生变化;存放12个月后发光强度降低0.7%;酸碱处理5min后发光强度降低超过10%,但发光波长均未发生改变。因此,在使用的过程中尽量保持存储环境的干燥,避免酸碱的长时间侵蚀。

关键词: 防伪, 纤维, 防伪特性, 稀土

Abstract: To promote the application and popularization of spectrum-fingerprint anti-counterfeiting fiber, in this paper, 9 kinds of fiber samples were prepared and the anti-counterfeiting characteristics of the fiber were studied with the help of fluorescence spectrophotometer. The results showed that spectrum-fingerprint fibers made by different raw materials and spinning process parameters had different emission spectra when excited with specific exciting light, which were unique, just like the fingerprint of human beings. The emission spectral curve of spectrum-fingerprint fiber had excellent reproducibility after repeated measurement and had no observable change happening after being stored for 6months, washed for 2hours, light for 5hours or being treated for 2hours by 120℃ tempreture, acide or base for 2minutes. But the emission intensity decreased by 0.7% after being stored for 12months and by over 10% after being treated by acide or base for 5minutes,meanwhile the emission wavelength had no change. Therefore the fiber should be stored in a dry environment and prolonged treatment should be avoided in application.

Key words: anti-counterfeiting, fiber, anti-counterfeiting characteristic, rare earth

[1] 葛明桥,赵菊梅,李永贵.一种防伪专用稀土发光纤维:中国, 200710133387.8[P].2008-03-12.
GE Mingqiao, ZHAO Jumei, LI Yonggui. An anti-counterfeiting rare-earth luminescent fiber: China patent, 200710133387.8[P]. 2008-03-12.
[2] 张技术,葛明桥.光谱指纹纤维的制备方法及其防伪原理[J]. 纺织学报,2011,32(6):7-11.
ZHANG Jishu,GE Minqiao. manufacturing technique and security principle of an anti-counterfeiting fiber with spectrum-fingerprint characteristics[J]. Journal of Textile Research, 2011,32(6):7-11.
[3] 张慧茹,黄素萍,龚静华,等. 荧光防伪纤维[J]. 合成纤维工业,2002,25(4):39-41.
ZHANG Huiru, HUA Suping, GONG Jinghua, et al. Fluorescent falsification-preventing fiber[J]. China Synthetic Fiber Industry, 2002, 25(4): 39-41.
[4] 龚静华, 黄素萍, 秦伟. 双波长荧光防伪纤维的研究[J]. 上海纺织科技,2002,30(5):14-15.
GONG Jinghua, HUANG Suping, QIN Wei. Study on biwavelength fluorescent falsification-proof fiber for identification[J]. Shanghai Textile Science & Technology, 2002, 30 (5): 14-15.
[5] 刘光华. 稀土材料及其应用技术[M]. 北京:化学工业出版社,2005:25-29.
LIU Guanghua. Rare-earth Materials and Application Technology [M]. Beijing: Chemical Industry Press, 2005: 25-29.
[6] 孙继兵,王海容,安雅琴,等。 长余辉发光材料研究进展[J].稀有金属材料与工程,2008,37(2):189-192.
SUN Jibing, WANG Hairong, AN Yaqin, et al. Progress on Long Persistence Luminescent Materials[J]. Rare Metal Materials and Engineering, 2008, 37(2): 189-192.
[7] QIU Guanming(邱关明), CHEN Yongjie(陈永杰), CUI Jingqiang(崔景强), et al. Synthesis of long afterglow phosphors doped B SrA1204: Eu2+, Dy3+ and its luminescent properties[J]. Journal of Rare Earths, 2007, 25, (Suppl,): 86-89.
[8] ZHANG Jishu,GE Minqiao. Effecting factors of the emission spectral characteristics of rare-earth strontium aluminate for anti-counterfeiting application[J]. Journal of Luminescence, 2011,131(8):1765-1769.
[9] ZHANG Jishu,GE Minqiao. Effect of polymer matrix on the on the spectral properties of spectrum-fingerprint anti-counterfeiting fiber[J]. The Journal of Textile Institute, 2012, 103(2):193-199.
[1] 曾婵娟 籍晓倩 刘雯雯 殷允杰 王潮霞. 10,12-二十五碳二炔酸改性聚氨酯/聚环氧乙烯纤维膜制备及其紫外光/热致变色性能[J]. 纺织学报, 2018, 39(08): 9-14.
[2] 高世会 郁崇文. 罗布麻中黄酮的超临界CO2萃取及其抗菌性[J]. 纺织学报, 2018, 39(08): 71-76.
[3] 杨文权 蒋金华 陈南梁. 玻璃纤维织物在剪切变形作用下的渗透率[J]. 纺织学报, 2018, 39(08): 58-62.
[4] 韦树琛 丁欣 李文霞 王华平 张朔. 废旧聚酯纤维制品近红外定量分析模型的建立及验证[J]. 纺织学报, 2018, 39(07): 63-68.
[5] 王航 庄旭品 董锋 石磊 康卫民 徐先林 程博闻. 溶液喷射纺纳米纤维制备技术及其应用进展[J]. 纺织学报, 2018, 39(07): 165-173.
[6] 吴小娟 余妙晶 舒慧 郑怡筱 葛烨倩 . 过温保护层合纳米纤维隔膜的制备及其性能[J]. 纺织学报, 2018, 39(07): 21-26.
[7] 陈洪立 焦晓宁 柯鹏. 取向增强复合锂离子电池隔膜的制备及其性能[J]. 纺织学报, 2018, 39(07): 8-14.
[8] 张博亚 李佳慧 张如全 李建强. 静电纺聚丙烯腈/硫酸铜纳米纤维膜的制备及其性能[J]. 纺织学报, 2018, 39(07): 15-20.
[9] 赵宝宝 钱晓明 钱幺 范金土 封严 朵永超. 水性聚氨酯机械发泡涂层的响应面法优化制备[J]. 纺织学报, 2018, 39(07): 95-099.
[10] 杨瑞华 韩瑞叶 徐亚亚 薛元 王鸿博 高卫东. 数码转杯纺混色纱中有色纤维混合效果分析[J]. 纺织学报, 2018, 39(07): 32-38.
[11] 姚勇波 颜志勇 李喆 易洪雷 张玉梅 王华平. 牵伸倍率分配对纤维素/丝素蛋白共混纤维形态结构的影响[J]. 纺织学报, 2018, 39(06): 13-18.
[12] 靳宏 刘怡宁 陈思 王乐军 张玉梅 王华平 . 相变Lyocell纤维制备中微胶囊相变材料与溶剂的相互作用[J]. 纺织学报, 2018, 39(06): 1-5.
[13] 马晓红 檀江涛 秦志刚. 碳纤维二维编织管状织物的编织工艺[J]. 纺织学报, 2018, 39(06): 64-69.
[14] 陈丽丽 楼利琴 傅雅琴. 木棉纤维/棉混纺织物结构参数对其保暖透气性影响[J]. 纺织学报, 2018, 39(06): 47-51.
[15] 何晓昀 韦平 张林 邓斌攸 潘云峰 苏真伟. 基于深度学习的籽棉中异性纤维检测方法[J]. 纺织学报, 2018, 39(06): 131-135.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!