高速纺丝油剂用丁醇聚醚链末端基的稳定性

  

  • 收稿日期:2014-10-27 修回日期:2015-08-17 出版日期:2015-11-15 发布日期:2015-11-10

Stability of terminal group of butanol polyether chain used as high-speed spinning finishes

  • Received:2014-10-27 Revised:2015-08-17 Online:2015-11-15 Published:2015-11-10

摘要:

高速纺丝油剂用丁醇聚醚链末端羟基在碱性及高温等条件下易于发生脱水反应从而影响丁醇聚醚的结构和高速纺丝油剂的使用性能。本课题研究丁醇聚醚生产、储运及使用条件对丁醇聚醚链末端基稳定性的影响。结果表明:氧气会加剧丁醇聚醚链末端基的不稳定性,有氧加速试验中丁醇聚醚双键含量增加幅度为0.0085%-0.0492%(即原料双键含量的1.0-5.4倍),明显大于氮气加速试验中双键含量的增加幅度。温度对丁醇聚醚链末端基稳定性影响显著,高温试验中丁醇聚醚双键含量增加幅度为0.0744%-0.1298%(即原料双键含量的8.1-14.1倍)。丁醇聚醚中含有的醛在碱性环境中会发生羟醛缩合反应生成烯醛,碱性试验中丁醇聚醚双键含量最大增加幅度为0.0114%-0.0255%(即原料双键含量的1.2-2.8倍)。

Abstract:

Dehydration of the end hydroxyl group of butanol polyether used as high-speed spinning finishes would occur under situations of alkalis or high temperatures, which lead to polyether’s structure and high-speed spinning finishes’ performances changes. This paper investigated terminal group’s stability of butanol polyether during processes of production, transportation, storage and usage. Results show that the end hydroxyl group of butanol polyether tends to be more unstable within oxygen. The increase range of double bond content within oxygen is 0.0085%-0.0492% (1.0-5.4 times higher than that of the original polyether), which is obviously larger than that within nitrogen. The polyether appears to be more unstable under high temperatures. The double bond content increases considerably with the growth in high temperatures showing 8.1-14.1 times higher than that of the original butanol polyether. The increase range of double bond content is 0.0744%-0.1298%. Olefine aldehyde was introduced through the Aldol condensation reaction in alklinities and the maximum increase of double bond content is 1.2-2.8 times higher compared with the original polyether. The increase range of double bond content is (0.0114%-0.0255%)

中图分类号: 

  • TQ326.5
[1] 李倩 周凯 尹红 陈志荣 袁慎峰. 高速纺丝油剂用丁醇聚醚主链的稳定性[J]. 纺织学报, 2015, 36(12): 75-0.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
[1] 管映亭;董政娥;金志浩. 纳米材料及其在纺织等领域中的应用[J]. 纺织学报, 2004, 25(03): 116 -118 .
[2] 汤加乐;李庆民. 减少纺织品火灾事故的对策初探[J]. 纺织学报, 1986, 7(04): 62 -64 .
[3] 毛莉莉;徐青青. 针织服装拉链缝制工艺[J]. 纺织学报, 2005, 26(5): 117 -119 .
[4] 王兟;张知佑. 转杯纺成纱强力及缠绕纤维百分率的研究[J]. 纺织学报, 1991, 12(11): 8 -11 .
[5] 黄起尚;黄焱. 改善苧麻棉型短纤混纺纱条干和强力的实践[J]. 纺织学报, 1990, 11(04): 39 -40 .
[6] 吴迪冲;顾新建. 服装大规模定制及其结构体系研究[J]. 纺织学报, 2004, 25(05): 139 -141 .
[7] 吴之传;汪学骞;陶庭先;毕松海;冯浩. 螯合金属离子的腈纶纤维的制备及性能[J]. 纺织学报, 2004, 25(06): 36 -37 .
[8] 毕可贤;冷玉梅. 柞蚕丝素溶解方法的研究[J]. 纺织学报, 1982, 3(11): 23 -26 .
[9] 钱铁钧. 用二氧化碳气体保护焊修理织机曲轴[J]. 纺织学报, 1986, 7(05): 50 .
[10] 叶雅君;傅继树. 变色羊毛绒线的研制[J]. 纺织学报, 1990, 11(03): 26 -27 .