Preparation of PVA/CS/Ce(NO3)3 blend fiber felt and its applications to Cr(Ⅵ) ions

 LU  Li-Ping, WANG  Fang-Fang, WU  Min   

  1. Key Laboratiry of Eco-Textiles (Jiangnan University), Ministry of Education
  • Received:2011-04-18 Revised:2012-01-11 Online:2012-05-15 Published:2012-05-15
  • Contact: WU Min E-mail:xycwxdq@sina.com

PDF (PC)

501

Abstract: The blend solution of polyvinyl alcohol(PVA) and chitosan(CS) and cerous nitrate(Ce(NO3)3) dissolving in dilute acetic at different mass ratios was spun into PVA/CS/Ce(NO3)3 blend fiber felt via electrospinning process.Using scanning electron microscopy and infrared spectrum on the adsorption of samples before and after the plating. Studied pH、time and concentration for Cr(Ⅵ) adsorption influence.Results show:the adsorption of metal ions were binding of metal ions to the chelating sites on the blend fiber felt,the effect of adsorption was the best when pH=4,the adsorption data of Cr(Ⅵ) were fitted well with langmuir isotherm,the equilibrium adsorption capacities were 59.81mg/g,the dispel of Cr(Ⅵ) can reach 87%.

Key words: electrospinning, chitosan, adsouption, Cr(Ⅵ)ion

[1] . Effect of modified by β-cyclodextrin derivatives of aldehydes crosslinked chitosan on hydrophilicity of polyester fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 82-88.
[2] . Preparation and properties of orientation reinforced composite separator for lithium-ion battery [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 8-14.
[3] . Preparation technology and application progress of solution blown nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 165-173.
[4] . Preparation and properties of collagen/high-molecular weight chitosan composite fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(05): 8-13.
[5] . Preparation and properties of electrospun polyacrylonitrile nanofiber coated window screen [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 14-18.
[6] . Preparation and antibacterial and dyeing properties of chitosan grafted antibacterial viscose fiber  [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 9-13.
[7] . Overview on mass production of electrospun nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(03): 175-180.
[8] . Oil absorption property of electrospun superfine fibrous membrane [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 7-13.
[9] . Electrospun barium titanate/ poly(vinylidene fluoride) nano-composite flexibility piezoelectric fibrous membranes [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(02): 14-19.
[10] . Preparation of crosslinking and high performance polymers [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(01): 6-10.
[11] . Effects of coaxial electrospinning parameters on morphology and carbonization yield of polyacrylonitrile hollow carbon nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(12): 1-6.
[12] . Research Progress in preparation and application of electrospinning porous carbon nanofibers [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 168-176.
[13] . Preparation of ultrafine polyacrylonitrile nanofibers via composite electrospinning [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 16-21.
[14] . Synthesis of fluorinated polyurethane and acid-proofness and water permeability of electrospun nanofiber membrane composite fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(10): 7-12.
[15] . In fluence of hydrogen bonding on electrospinning of starch nanofiber in dimethyl sulfoxide/H2O solution [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 19-23.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd