Antistatic effect of PET fabrics finished with mixture of nano ZnO & Fe2O3 sol

  

  • Received:2012-03-09 Revised:2013-01-14 Online:2013-04-15 Published:2013-04-09

PDF (PC)

384

Abstract: Several nanometer ZnO-Fe2O3 sols with different molar ratios were made up from Zn(CH3COO)2?2H20 and FeCl2?4H2O mixture, which is the raw material by sol-gel method in this experiment. The PET fabric was treated with the nanometer ZnO-Fe2O3 hybrid sol by padding-baking process. Then, the antistatic effect of different molar ratio was studied. The experiment shows that the best antistatic molar ratio of the Zn(CH3COO)2?2H20 and FeCl2?4H2O is 5:1, and meanwhile half-life and peak voltage decreased from 11.31sec and 860v to 0.

Key words: nano ZnO, nano Fe2O3, sol-gel, antistatic, PET fabric

CLC Number: 

  • TS195.5
[1] . UV-induced grafting dyeing of modified reactive dye on alkali treated polyester fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(11): 91-96.
[2] . Research progress of new processes of flame retardant fabrics coating [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(09): 168-173.
[3] . Flame retardant finishing of silk fabrics with boron phosphate doped silica sol [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(08): 96-101.
[4] . Synthesis and properties of hydrophilic antistatic polyester masterbatch by melt blending [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(07): 6-10.
[5] . Preparation and characterization of cotton-like poly(ethylene terephthalate) fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2015, 36(02): 19-0.
[6] . Removal of polyacrylate size from PET fabric by combination of plasma and wet desizing [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(1): 78-0.
[7] Yun-Jie YIN. Preparation and properties of hydrophobic-hydrophilic switchable coating via UV radiation on cotton fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(2): 120-124.
[8] . Preparation of nanoscale SiO2/PSSS composite particles by in-situ polymerization and their properties [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(11): 6-0.
[9] . Analysis of nano-particle size in fibroin membrane modified by nano TiO2 [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(11): 24-0.
[10] . Process for preparing Sb-doped tin dioxide film on surface of glass fiber by sol-gel method [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(11): 11-0.
[11] LIU Xiao-Yun, WANG Xiao-Fang, ZHOU Lan. Antistatic properties of PDMDAAC/AM on polyester fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(8): 92-96.
[12] . Synthesis of nano-SiO2/PSt via miniemulsion polymerization and modification of polyacrylate sizing with it [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(11): 66-71.
[13] . Effect of annealing temperature on the conductive and optical properties of SnO2 thin film coated on glass fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(11): 37-41.
[14] TANG Junyun;DI Jianfeng. Advances in the research of PANI composite conductive fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(3): 148-152.
[15] ZHOU Zhaoyi;ZHAO Yaping;GE Fengyan;CAI Zaisheng. Low-temperature solution growth of ZnO nanorods on PET fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(7): 6-10.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd