纺织学报 ›› 2018, Vol. 39 ›› Issue (02): 97-105.doi: 10.13475/j.fzxb.20171000809

• 染整与化学品 • 上一篇    下一篇

一体化聚氨酯丙烯酸酯的合成及其在光固化数码印花中的应用

  

  • 收稿日期:2017-10-09 修回日期:2017-11-17 出版日期:2018-02-15 发布日期:2018-02-11

Synthesis of integrated polyurethane acrylate and application thereof in photo-curable ink-jet printing

  • Received:2017-10-09 Revised:2017-11-17 Online:2018-02-15 Published:2018-02-11

摘要:

为改善光固化数码印花织物的安全性、手感与牢度,设计合成了有机硅氨基改性光敏聚氨酯丙烯酸酯低聚物,并对其流变性能,光聚合性能,以及固化膜物理力学及光学等性能进行测试分析。研究结果表明:该聚氨酯丙烯酸酯兼具低黏、低模量、高柔弹和助引发一体化功能。有机硅氨基改性光敏聚氨酯丙烯酸酯共聚膜因其有机硅链段向膜表面迁移,当有机硅含量为5%时其固化膜力学性能损失小且具有较好的柔顺性和耐水性。以合成的改性聚氨酯丙烯酸酯和丙烯酸羟乙酯复配构建光固化聚合体系,配制光敏剂樟脑醌、着色剂颜料及相关助剂,制备光固化数码喷墨印花墨水,其最终转化率为96%,可见光透过率大于95%,拉伸应力为1.5 MPa,最大断裂伸长率为530%,100%伸长应力低于0.4 MPa。应用光固化数码喷墨印花制备的织物,其摩擦牢度可达4级。

关键词: 聚氨酯丙烯酸酯, 光固化, 数码喷墨印花, 印花墨水

Abstract:

A series of organosilicone and amino modified photosensitive polyurethane acrylates (PUA) were designed and synthesized for improve the safety, handeling and rubbing fastness of photo-curable ink-jet printing fabrics. According to the research of the rheological properties, photo initiated properties, tensile properties, optical properties and SEM analysis, the polyurethane acrylate has integrated function of low viscosity and modulus, high flexibility and co-initiation. While curing, the copolymer siloxane chain segments migrated to the film surface. The cured film has better flexibility and water resistance while the mechanical property loss is  small when the content of organosilicone is 5%. The photo-curable ink-jet printing ink was prepared successfully by mixing a photocurable polymerization system composed of the modified PUA and hydroxyethyl acrylate, 2-Hydroxyethyl acrylate, camphorquinone and other additives, and has the conversion rate os 96%, the transparency above 95%, the tensile stress of 1.5 MPa, the maximum elongation at break of 530%, and 100% elongation stress lower than 0.4MPa, low toxicity and good stability. The fabric subjected to the photo curing Ink-jet printing ink has good rubbing fastness up to grate 4.

Key words: polyurethan acrylate, photocuring, digital ink-jet printing, printing ink

[1] 蓝杰蕊 沈锦玉 李玖明 陈建勇 郭玉海 张华鹏 . 紫外光固化技术对聚丙烯非织造布的亲水改性[J]. 纺织学报, 2017, 38(05): 98-103.
[2] 杨帆 陈远辉 顾晨成 冒海燕 王潮霞 殷允杰. 紫外光固化水性聚氨酯丙烯酸酯黏合剂的印花性能[J]. 纺织学报, 2016, 37(3): 82-0.
[3] 邵建中 黄益. 用于纺织品数码印花的蓝光固化聚合体系性能研究[J]. 纺织学报, 2015, 36(02): 121-0.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!