织物结构对安芙赛纺织品阻燃性能的影响

郑振荣;顾振亚;杨文芳;王乐军   

  • 收稿日期:1900-01-01 修回日期:1900-01-01 出版日期:2009-02-15 发布日期:2009-02-15

Effect of fabric structures on the flame retardant property of Anti-fcell® fabrics

ZHENG Zhenrong;GU Zhenya;YANG Eenfang;WANG Lejun   

  • Received:1900-01-01 Revised:1900-01-01 Online:2009-02-15 Published:2009-02-15

摘要: 为提高安芙赛阻燃纤维织物的阻燃性能,采用极限氧指数法研究机织物纱线线密度和捻度、织物组织、经密、织物面密度等参数对其织物阻燃性能的影响。结果表明:双层织物的阻燃性能优于单层织物,极限氧指数均大于31.0%;双层织物的密度、纱线线密度、捻度越大,极限氧指数越高。此外,对安芙赛非织造布阻燃性能的研究结果表明:安芙赛非织造布极限氧指数随面密度的增加而提高;当安芙赛纤维与阻燃涤纶混合制备非织造布时,安芙赛纤维的含量应高于60%;当安芙赛纤维与羊毛纤维混合制备阻燃非织造布时,安芙赛纤维的含量应高于25%。

Abstract: To improve the flame retardant property of Anti-fcell® flame retardant fabric, the effects of yarn linear density, twist, structure, warp density, and surface density etc on Anti-fcell® fabrics’ flame retardant (FR) property were investigated using Limiting Oxygen Index (LOI) test. The results showed that the FR property of the double-layer fabrics were better than that of the monolayer fabrics. The LOI value of these double-layer fabrics were all above 31.0%. Higher the density, yarn linear density and twist of the double-layer fabric, better its FR property. In addition, the FR properties of Anti-fcell®/FR-PET and Anti-fcell®/wool mixed nonwoven fabric were investigated. It was found that the LOI value of Anti-fcell®/FR-PET mixed nonwoven fabric was higher than 26% when Anti-fcell® fiber contained more than 60%. And the LOI of Anti-fcell®/wool mixed nonwoven fabric was higher than 26.5% when Anti-fcell® fiber contained more than 25%.