Degumming of lotus fiber and its property

ZHANG Hongwei; LI Yonglan; LI Nan; WANG Mingfang; YUAN Hongping   

  • Received:1900-01-01 Revised:1900-01-01 Online:2009-06-15 Published:2009-06-15

摘要: 以食用藕的荷叶茎杆为原料,采用河水浸渍和碱煮脱胶的方法制取莲纤维。对莲纤维的组成成分、回潮率、密度、线密度、强度、断裂伸长率等性能指标进行了测试分析;结合IR、XRD、SEM等测试方法,对莲纤维的组成成份和结构进行分析和表征。结果表明,所制取的莲纤维组成成分与黄麻相似,属于天然纤维素纤维。得出最优的碱煮精制工艺为:NaOH质量浓度10g/L、温度100℃、时间3h。精制莲纤维具有一定的纺纱性能,平均直径317μm、线密度55.8 dtex、强度1.76cN/dtex、强度变异系数40.2%、断裂伸长率7.84%,但还有待于进一步细化和增强。

Abstract: Take the edible lotus leaf and stalk as raw material, lotus fiber was produced by degumming methods such as river retting and sodium hydroxide boiling. The components and properties of the fiber, such as moisture regain, density, linear density, strength and break elongation, were tested. Infrared spectroscopy (IR), X-ray diffractometer (XRD), scanning electron microscope (SEM) were use to characterize the components and structure of lotus fiber. The results show that the components of obtained lotus fiber are similar to those of jute, and belong to natural cellulose fiber. The optimized sodium hydroxide boiling technology for the fiber: NaOH concentration is 10 g/L, boiling at 100℃ for 3 hours. The produced lotus fiber, with diameter 317μm, linear density 55.8dtex, strength 1.76cN/dtex, strength variation coefficient 40.2% and break elongation 7.84%, is spinnability. However, the fiber’s linear density and strength should be improved further.

No related articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!