The effects of the texturing entropy change on the bending stiffness of textured yarn

 JIANG  Yan, JIANG  Li, WANG  Shan-Yuan   

  • Received:2011-05-05 Revised:2011-09-24 Online:2012-03-15 Published:2012-03-06

摘要: 长纤复丝经变形加工,其结构系统熵值增大,这一现象往往与长复丝系统抗弯刚度的变化伴随发生。采用悬臂梁方法测试变形纱抗弯刚度,采用EIB测量变形纱直径而后测算变形纱相对熵值,可对变形加工过程中线性体发生的熵变现象和抗弯刚度变化的关系进行定量分析。经测试,空气变形加工可使成纱相对熵值由0.3增加到1.45,紊乱度由1.28增加到4.25;再经异收缩多重变形相对熵值可增加到1.65,而紊乱度可增加到5.00左右。长丝片段紊乱度增加直接导致空气变形类纱线紊乱结构和缠结结构的形成与扩大,在宏观上呈现纱线抗弯刚度的迅速增大,从而进一步导致纱线手感变坏;多重变形有可能使已形成的纱线缠结结构得到调整,从而使纱线抗弯刚度下降。

Abstract: During the course of texturing, the entropy of the filaments structure system was increased. Corresponding changes in its bending stiffness always occurred with this phenomenon at the same time. To quantitative analyze the relationship between the entropy changing and stiffness changes of a linear model during texturing, cantilever measuring was used to measure the bending rigidity of the textured yarns while the EIB to test their diameter and then the relative entropy value were told. The results showed that air-texturing could rise the relative entropy value from 0.3 to 1.45 while the disordering degree 1.28 to 4.25; further differential shrinking would increase the relative entropy value to 1.65, as well the disordering degree to 5.00 and so on. The increasing disordering degree of the filaments’ fragments led to the forming and enlarging of the disordering structure and entanglement structure, which was shown by the rapid rising of bending stiffness and worse handle of ATY; by multi-texturing the entanglement structure might be adjusted and lower bending stiffness might be then.