Hand feeling comparison between PTT and nylon fabrics under cold environmental condition

LI Rong-Quan¹, WANG Fu-Mei¹, ZHANG Li-Zhi²

1. College of Textiles,Donghua University
2. DuPont (China) Research & Development and Management Co. , Ltd.

Received:2011-06-18 Revised:2012-04-16 Online:2012-07-15 Published:2012-07-02
Contact: WANG Fu-Mei E-mail:wfumei@dhu.edu.cn

摘要/Abstract

摘要： 摘要为了探索在低温环境下使用的羽绒服和防寒服等服装的理想面料，需要研究这些面料的手感随着环境温度的变化所呈现出的规律。在现有试验条件下，测试温度分别设定在20℃、-5℃、-15℃、-25℃四个点，通过自行搭建的可在低温下测试的简易装置对比测试并研究了结构参数相近的PTT织物和锦纶织物的弯曲性能和剪切性能，以描述织物的手感变化和差异。结果表明，随温度降低，两类织物的手感都会变得僵硬，但锦纶织物变硬的程度比PTT织物要大许多。

关键词: PTT织物 , 锦纶织物 , 低温环境 , 手感 , 弯曲性能 , 剪切性能

Abstract: Abstract In order to explore the ideal apparel fabrics for down jackets and cold resistance clothes that can be used in extremely cold environment and the changes of hand with the temperature decreased. The bending and shearing performances of two types of fabrics are studied by the in-house made test device at 20℃,-5℃,-15℃,-25℃respectively. The structure parameters of the PTT fabric and Nylon fabric are similar. The results show that the hand of the two types of fabrics become more stiff with the temperature decreased. However, Nylon fabric becomes much stiffer than PTT fabric at the same temperature.

Key words: PTT fabric , nylon fabric , cold environmental condition , hand feeling , bending property , shearing property

李荣全, 王府梅, 张丽芝. 低温环境下PTT与锦纶织物的手感比较[J]. 纺织学报, 2012, 33(7): 53-57.

LI Rong-Quan, WANG Fu-Mei, ZHANG Li-Zhi. Hand feeling comparison between PTT and nylon fabrics under cold environmental condition[J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(7): 53-57.

参考文献

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed

[1]	张艳明;姜亚明;邱冠雄;刘良森. 纬编双轴向多层衬纱织物的双半球成型性[J]. 纺织学报, 2005, 26(3): 54-56.
[2]	徐广标;王府梅;陈小萱. 精纺毛型织物剪切性能的实验研究[J]. 纺织学报, 2004, 25(03): 34-36.