Structure and properties of keratin film modified by carboxymethyl cellulose sodium

LIU Shuping1,2,3(), LI Liang2,3,4, LIU Rangtong1,2,3, CUI Shizhong2,3,4, WANG Yanting2,3,4   

  1. 1. The School of Fashion Technology, Zhongyuan University of Technology, Zhengzhou, Henan 450007, China
    2. Henan Provincial Collaborative Innovation Center of Textile and Clothing, Zhengzhou, Henan 450007, China
    3. Henan Provincial Key Laboratory of Functional Textile Materials, Zhengzhou, Henan 450007, China
    4. The School of Textiles, Zhongyuan University of Technology, Zhengzhou, Henan 450007, China
  • Received:2018-07-04 Revised:2019-03-09 Online:2019-06-15 Published:2019-06-25

Abstract:

In order to improve film-forming properties of keratin, carboxymethyl cellulose sodium (CMCNa) was used as the modifier and blended with wool keratin to prepare a wool keratin film. The performances of the modified film were characterized by laser microscopy, infrared spectroscopy, X-ray diffraction, thermal properties, etc. The results indicate that the addition of CMCNa makes the structure of keratin membrane much denser, and improves its thermal stability and hydrophobicity. Moreover, its elongation increases from 1.8% to 6.4%, and its degradation in water also increases from 20.4% to 78.6%. However, its strengthen decreases from 35 MPa to 16.3 MPa. The reason is that inter-molecular hydrogen bond interaction between CMCNa and keratin occurs during the blending process, which reduces the intra-molecular hydrogen bonding of keratin. Further, with the addition of CMCNa, the crystal structure of modified membrane changes from the alpha-helical structure of wool keratin to the structure of both alpha-helical and beta-folded crystals.

Key words: wool keratin film, carboxymethyl cellulose sodium, modified film, crystalline structure, mechanical property

CLC Number: 

  • TS102.3

Fig.1

Modified mechanism of wool keratin film by carboxymethyl cellulose sodium"

Fig.2

Surface morphologies of keratin film (a) and CMCNa modified film (b)(×1 000)"

Fig.3

Infrared spectra of keratin film, CMCNa film and modified film"

Fig.4

XRD crystal structure of keratin film, CMCNa film and modified film"

Fig.5

Thermo-gravimetric curves of keratin film (a) and CMCNa modified film (b) at different temperatures"

Fig.6

Change curves of contact angle of keratin film and CMCNa modified film at different time"

Fig.7

Tensile curves of keratin film and CMCNa modified film"

[1] 邓湘文, 尹国强, 张步宁, 等. 热压羽毛角蛋白膜的制备及性能表征[J]. 化工新型材料, 2015,43(8):60-62.
DENG Xiangwen, YIN Guoqiang, ZHANG Buning, et al. Preparation and property of compression-molding feather keratin films[J]. New Chemical Materials, 2015,43(8):60-62.
[2] ROUSE J G, VAN D M E. A review of keratin-based biomaterials for biomedical applications[J]. Materials, 2010,3(2):999-1014.
[3] CARDAMONE J M. Investigating the microstructure of keratin extracted from wool: peptide sequence (MALDI-TOF/TOF) and protein conformation (FTIR)[J]. Journal of Molecular Structure, 2010,969:97-105.
[4] 袁祖纯, 黄水旺, 吴红熹, 等. 羊毛角蛋白膜的制备和热性能分析[J]. 纺织科技进展, 2012(2):36-38.
YUAN Zuchun, HUANG Shuiwang, WU Hongxi, et al. Preparation of wool keratin film and analysis of its thermal property[J]. Progress in Textile Science & Technology, 2012(2):36-38.
[5] 张恒, 李戎, 王魁, 等. 还原法与离子液体溶解法制备羊毛角蛋白膜[J]. 纺织学报, 2015,36(6):55-59.
ZHANG Heng, LI Rong, WANG Kui, et al. Preparation of wool keratin membranes prepared by ionic liquid method and reduction C method[J]. Journal of Textile Research, 2015,36(6):55-59.
[6] 潘军强, 姚金波, 贾书刚. 羊毛角蛋白/PVA共混薄膜的性能分析[J]. 毛纺科技, 2015,43(3):25-28.
PAN Junqiang, YAO Jinbo, JIA Shugang. The performance analysis of wool keratin/PVA hybrid film[J]. Wool Textile Journal, 2015,43(3):25-28.
[7] 张玉荣, 刘建勇, 王洁. 乙二醇二缩水甘油醚交联羊毛角蛋白[J]. 材料导报, 2013,27(21):230-232.
ZHANG Yurong, LIU Jianyong, WANG Jie. Cross-linking of wool's keratin by ethylene glycol diglycidyl ether[J]. Materials Review, 2013,27(21):230-232.
[8] 李慧, 卢立新, 王利强. 海藻酸钠-羧甲基纤维素钠-明胶共混膜的结构及性能研究[J]. 食品科学, 2010(5):91-95.
LI Hui, LU Lixin, WANG Liqiang. Structure and properties of sodium alginate-sodium carboxymethyl cellulose gelatin compound film[J]. Food Science, 2010(5):91-95.
[9] 曾春慧, 张延林, 刘春光, 等. 改性羊毛角蛋白复合膜的性能与结构[J]. 中国皮革, 2014,43(23):13-18.
ZENG Chunhui, ZHANG Yanlin, LIU Chunguang, et al. Structure and properties of modified wool keratin composite membrane[J]. China Leather, 2014,43(23):13-18.
[10] WANG Ming, ZHAO Tao, WANG Gehui, et al. Blend films of human hair and cellulose prepared from an ionic liquid[J]. Textile Research Journal, 2014,84(12):1315-1324.
[11] HUSON M, CHURCH J S, HEINTZE G. Spectroscopy, microscopy and thermal analysis of the bi-modal melting of Merino wool[J]. Wool Technology and Sheep Breeding, 2002,50(1):64-75.
[12] 苟明霞. 羊毛角蛋白膜的制备及其结构性能的研究[D]. 苏州: 苏州大学, 2011: 23-32.
GOU Mingxia. Preparation and study on the structure and properties of wool keratin films[D]. Suzhou: Soochow University, 2011: 23-32.
[13] CHO H J, BALAKRISHNAN P, SHIM W S, et al. Characterization and in vitro evaluation of freeze-dried microparticles composed of granisetron-cyclodextrin complex and carboxymethyl cellulose[J]. International Journal of Pharmaceutics, 2010,400:59-65.
doi: 10.1016/j.ijpharm.2010.08.030 pmid: 20801202
[14] AYUTTHAYA S I, TANPICHAI S, WOOT-THIKANOKKHAN J. Keratin extracted from chicken feather waste: extraction, preparation, and structural characterization of the keratin and keratin/biopolymer films and electrospuns[J]. Journal of Polymers and the Environment, 2015,23:506-516.
[15] HAGEGE R, CONNET J. Thermal analysis and morphology of the heat degradation of wool and mohair[C]// 6th Quinquennial International Wool Textile Research Conference on Proceedings of the Structure and Chemical Reactions of Keratins.[s.n.]: Prectoria, 1980: 221-224.
[1] PANG Yali, MENG Jiayi, LI Xin, ZHANG Qun, CHEN Yankun. Preparation of graphene fibers by wet spinning and fiber characterization [J]. Journal of Textile Research, 2020, 41(09): 1-7.
[2] ZHAN Xiaoqing, LI Fengyan, ZHAO Jian, LI Haiqiong. Thermal mechanical stability of ultrahigh molecular weight polyethylene fiber#br# [J]. Journal of Textile Research, 2020, 41(08): 9-14.
[3] ZHANG Zhuhui, ZHANG Diantang, QIAN Kun, XU Yang, LU Jian. Weaving process and off-axial tensile mechanical properties of wide-angle woven fabric [J]. Journal of Textile Research, 2020, 41(08): 27-31.
[4] LIU Xi, WANG Dong, ZHANG Liping, LI Min, FU Shaohai. Effect of low refractive resin on structure and properties of spun-dyed viscose fibers [J]. Journal of Textile Research, 2020, 41(07): 9-14.
[5] LI Liping, WU Daoyi, ZHAN Yikai, HE Min. Review on carbon fiber surface modification using electrophoretic deposition of carbon nanotubes and graphene oxide [J]. Journal of Textile Research, 2020, 41(06): 168-173.
[6] WANG Zongqian, YANG Haiwei, ZHOU Jian, LI Changlong. Effect of urea degumming on mechanical properties of silk fibroin aerogels [J]. Journal of Textile Research, 2020, 41(04): 9-14.
[7] DING Fang, REN Xuehong. Flame-retardant finishing of polyester fabrics by grafting phosphorus-nitrogen compounds [J]. Journal of Textile Research, 2020, 41(03): 100-105.
[8] CUI Yifan, HOU Wei, ZHOU Qianxi, YAN Jun, LU Yanhua, HE Tingting. Influence of silk sericin temperature sensitive hydrogel on properties of cotton fabrics [J]. Journal of Textile Research, 2019, 40(12): 74-78.
[9] ZHANG Jiao, GAO Xuefeng, WANG Yuzhou, LIU Haihui, ZHANG Xingxiang. Preparation and properties of polyamide 66/amino-functionalized multi-walled carbon nanotubes fibers [J]. Journal of Textile Research, 2019, 40(11): 1-8.
[10] YANG Fan, LIU Junhua, BIAN Angting, WANG Yanping, QIAN Qiyuan, NI Jianhua, XIA Yumin, HE Yong, WANG Yimin. Influence of heat treatment on structure and properties of thermotropic liquid crystalline polyarylate fiber [J]. Journal of Textile Research, 2019, 40(11): 9-12.
[11] WU Liwei, WANG Wei, LIN Jiahorng, JIANG Qian. Preparation and mechanical properties of aramid/ ultra-high molecular weight polyethylene fabric reinforced polyurethane sandwich composite [J]. Journal of Textile Research, 2019, 40(07): 64-70.
[12] . Influence of multistage drawing and heat setting on structure and properties of polyethylene / polypropylene bicomponent fibers [J]. Journal of Textile Research, 2019, 40(05): 24-29.
[13] . Preparation and properties of poly(3-hydroxybutyrate-co-3-hydroxyl valerate) / polylactic acid flame retardant fibers [J]. Journal of Textile Research, 2019, 40(05): 12-17.
[14] . Preparation and properties of glass fiber / polypropylene fiber reinforced thermoplastic composites#br# [J]. Journal of Textile Research, 2019, 40(03): 71-75.
[15] . Mechanical properties of basalt plain fabric reinforced hot bonded puncture-resistant insoles composites#br# [J]. Journal of Textile Research, 2019, 40(03): 54-58.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!