JOURNAL OF TEXTILE RESEARCH ›› 2006, Vol. 27 ›› Issue (10): 6-8.
• 研究论文 • Previous Articles Next Articles
KANG Wei-min;CHENG Bo-wen;ZHUANG Xu-pin;DING Chang-kun
Received:
Revised:
Online:
Published:
Abstract: Spinning solution of poly(hexamethylene adipate)(13%) was prepared using 2∶1(w/w) mixture of 1,2-dichloroethane and trifluoroacetic acid as solvent at room temperature.Poly(hexamethylene adipate) was electrospun into nano_fiber whose diameter in the range of 80~(500 nm,) and the nano_fiber composite membrane with electret melt-blowing nonwovens was also presented.The morphology of the nano_fiber was investigated by SEM,and the filtration property of the nano_fiber composite membrane with electret melt-blowing nonwovens was examined.The results showed that the filtration efficiency of nano_fiber composite membrane with electret melt-blowing nonwovens to the particles diameter about(0.3 μm) at a flow rate of(2.83 L/min) reaches(99.9%.)
KANG Wei-min;CHENG Bo-wen;ZHUANG Xu-pin;DING Chang-kun. Electrospun nano-fiber composite membrane and its filtration properties[J].JOURNAL OF TEXTILE RESEARCH, 2006, 27(10): 6-8.
0 / / Recommend
Add to citation manager EndNote|Reference Manager|ProCite|BibTeX|RefWorks
URL: http://www.fzxb.org.cn/EN/
http://www.fzxb.org.cn/EN/Y2006/V27/I10/6
Cited