Journal of Textile Research ›› 2019, Vol. 40 ›› Issue (05): 12-17.doi: 10.13475/j.fzxb.20180605906

• Fiber Materials • Previous Articles     Next Articles

Preparation and properties of poly(3-hydroxybutyrate-co-3-hydroxyl valerate)/polylactic acid flame retardant fibersMO

MO Dajie1, LI Xuming1,2(), XU Zenghui3   

  1. 1. College of Textile and Garment, Shaoxing University, Shaoxing, Zhejiang 312000, China
    2. Key Laboratory of Clean Dyeing and Finishing Technology, Shaoxing University, Shaoxing, Zhejiang 312000, China
    3. Jiangnan Branch, China Textile Academy, Shaoxing, Zhejiang 312071, China
  • Received:2018-06-20 Revised:2019-01-28 Online:2019-05-15 Published:2019-05-21
  • Contact: LI Xuming E-mail:lixm@usx.edu.cn

RichHTML

8

PDF (PC)

62

Abstract:

In order to prepare the biodegradable fiber with flame retardant property, poly(3-hydroxybutyrate-co-3-hydroxyl valerate)(PHBV), poly(lactic acid)(PLA) and ammonium polyph osphate(APP) were melt blended, then PHBV/PLA/APP composite fiber was prepared by melt spinning. The thermal property, heat stability, tensile property and flame retardant properties of PHBV/PLA/APP composite fiber were tested. The results show that the addition of APP has no significant effect on the cool crystallization temperature and melting temperature of PHBV/PLA. With the increasing of APP mass fraction, thermal stability and carbon yield of PHBV/PLA composite are improved. With the increasing of draft ratio, the breaking strength of PHBV/PLA/APP composite fiber is enhanced. The breaking strength of PHBV/PLA/APP composite fiber is firstly increased then decreased with the addition of APP. When the APP mass fraction is 5%, the breaking strength reaches the peak value. Meanwhile, with the increasing of APP mass fraction, the flame retardant property of the composite fiber is improved. When the APP mass fraction is 10%, the flame retardant effect is optimum, the value of limit oxygen index is 32.3%, the flame retardant class is V-0, and no molten drop phenomenon occurs in burning process.

Key words: poly(3-hydroxybutyrate-co-3-hydroxyl valerate), polylactic acid, ammonium polyphosphate, melt spinning, mechanical property, flame retardant property

CLC Number: 

  • TS102.5

Fig.1

DSC heating curves of PHBV/PLA/APP composites"

Fig.2

TG(a) and DTG(b) curves of PHBV/PLA/APP composites"

Fig.3

Section surface morphologies of PHBV/PLA/APP composites with different APP contents (×500)"

Fig.4

Influence of draft ratio on breaking strength of PHBV/PLA/APP composite fibers"

Fig.5

Influence of APP content on tensile properties of PHBV/PLA/APP composite fibers"

Tab.1

Flame retardancy of PHBV/PLA/APP composites with different APP contents"

样品编号 LOI值/% UL94等级 有无熔滴
0# 23.6 V-2 有
1# 24.9 V-2 有
2# 28.5 V-1 有
3# 32.3 V-0 无
4# 32.7 V-0 无
[1] ZEMBOUAI Idris, KACI Mustapha, BEMHAMIDA Aida, et al. Poly(3-hydroxybutyrate-co-3-hydroxyvalerate)/poly-lactide blends: thermal stability, flammability and thermo-mechanical behavior[J]. J Polym Environ, 2014: 131-139.
[2] LI Longzhen, HUANG Wei, WANG Bingjie, et al. Properties and structure of polylactide/poly (3-hydroxy-butyrate-co-3-hydroxyvalerate) (PLA/PHBV) blend fibers[J]. Polymer, 2015,68:183-194.
[3] 朱斐超, 韩建, 于斌, 等. 熔喷非织造用聚(3-羟基丁酸-co-3-羟基戊酸共聚酯)/聚乳酸双组分生物降解材料的可纺性能[J]. 纺织学报, 2016,37(2):21-27.
ZHU Feichao, HAN Jian, YU Bin, et al. Study on spinnability of biodegradable poly(3-hydroxybutyrate-co-3-hydroxyl valerate) / poly (1actic acid) blends for melt-blown nonwovens[J]. Journal of Textile Research, 2016,37(2):21-27.
[4] JENNIFER G A, ESTEFANIA S S, JOSE M L, et al. Compatibilization of poly (3-hydroxybutyrate-co-3-hydroxy-valerate)-poly(lactic acid) blends with diisocyanates[J]. Journal of Applied Polymer Science, 2017(134):44806.
[5] 李旭明, 孙西超, 师利芬. 增强增韧聚乳酸纤维的制备及其性能[J]. 纺织学报, 2017,38(4):12-16.
LI Xuming, SUN Xichao, SHI Lifen. Preparation and properties research of reinforcing and toughening PLA fiber[J]. Journal of Textile Research, 2017,38(4):12-16.
[6] LIU Q, WU C, ZHANG H, et al. Blends of polylactide and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with low content of hydroxyvalerate unit:morphology,structure,and property[J]. Journal of Applied Polymer Science, 2015,132(42):42689.
[7] MA P, SPOELSTRA A B, SCHMIT P, et al. Toughening of poly(1actic acid) by poly(β-phydroxybutyrate-co-β-hydroxyvalerate) with high β-hydroxyvalerate content[J]. European Polymer Journal, 2013,49(6):1523-1531.
doi: 10.1016/j.eurpolymj.2013.01.016
[8] WANG Yuying, SHIH Yengfong. Flame-retardant recycled bamboo chopstick fiber-reinforced poly(lactic acid) green composites via multifunctional additive system[J]. Journal of the Taiwan Institute of Chemical Engineers, 2016 (65):452-458.
[9] ZHU H, ZHU Q, LI J, et al. Synergistic effect between expandable graphite and ammonium polyphosphate on flame retarded polylactide[J]. Polym Degrad Stab, 2011,96:183-189.
[10] MATK S, TOLDY A, KESZEI S, et al. Flame retardancy of biodegradable polymers and biocom-posites[J]. Polymer Degradation and Stability, 2005(88):138-145.
[11] HAPUARAEHEHI T D, PEIJS T. Multiwalled carbon nanotubes and sepiolite nanoclays as flame retardants for polylactide and its natural fibre reinforced compo-sites[J]. Composites Part A: Applied Science and Manufacturing 2010(41):954-963.
[12] SHUKOR F, HASSAN A, ISLAM M S, et al. Effect of ammonium polyphosphate on flame retardancy, thermalstability and mechanical properties of alkali treated kenaf fiber filled PLA biocomposites[J]. Material and Design 2014(54):425-429.
[13] VAHABI Henri, SHABANIAN Meisam, ARYANASAB Fezzeh, et al. Inclusion of modified lignocellulose and nano-hydroxyapatite in development of new bio-based adjuvant flame retardant for poly(lactic acid)[J]. Thermochimica Acta 2018(666):51-59.
[14] PRABHAKAR M N, REHMAN S A U, SONG J I, et al. Improved flame-retardant and tensile properties of thermoplastic starch/flax fabric green Composites[J]. Carbohydrate Polymers 2017(168):201-211.
[15] REALINHO Vera, HAURIE Laia, FORMOSA Joan, et al. Flame retardancy effect of combined ammonium polyphosphate and aluminium diethyl phosphinatein acrylonitrile-butadiene-styrene[J]. Polymer Degradation and Stability 2018(155):208-219.
[16] KHANAL Santosh, ZHANG Weipeng, AHMED Saad, et al. Effects of intumescent flame retardant system consisting of tris(2-hydroxyethyl) isocyanurate and ammonium polyphosphate on the flame retardant properties of high-density polyethylene composites[J]. Composites Part A: Applied Science and Manufacturing 2018(112):444-451.
[17] JEENCHAM Rachasit, SUPPAKAM Nitinat, JARUKUMJORN Kasama. Effect of flame retardants on flame retardant, mechanical, and thermal properties of sisalfiber/polypropylene composites[J]. Composites Part B: Engineering 2014(56):249-253.
[18] YANG Xing, ZHANG Wei. Flame Retardancy of Wood-Polymeric Composites[M]. Amsterdam: Elsvier, 2019: 285-317.
[19] WANG Ming, WU Ying, LI Yidong, et al. Progress in toughening poly(lactic acid) with renewable polymers[J]. Polymer Reviews 2017(57):557-593.
[1] GUAN Fucheng, GUO Jing, LÜ Lihua, TAN Qian, SONG Jingxing, ZHANG Xin. Hydrogen bonding mechanism and properties of polyvinyl alcohol / krill protein fibers [J]. Journal of Textile Research, 2020, 41(10): 7-13.
[2] PANG Yali, MENG Jiayi, LI Xin, ZHANG Qun, CHEN Yankun. Preparation of graphene fibers by wet spinning and fiber characterization [J]. Journal of Textile Research, 2020, 41(09): 1-7.
[3] ZHAN Xiaoqing, LI Fengyan, ZHAO Jian, LI Haiqiong. Thermal mechanical stability of ultrahigh molecular weight polyethylene fiber#br# [J]. Journal of Textile Research, 2020, 41(08): 9-14.
[4] ZHANG Zhuhui, ZHANG Diantang, QIAN Kun, XU Yang, LU Jian. Weaving process and off-axial tensile mechanical properties of wide-angle woven fabric [J]. Journal of Textile Research, 2020, 41(08): 27-31.
[5] LIU Xi, WANG Dong, ZHANG Liping, LI Min, FU Shaohai. Effect of low refractive resin on structure and properties of spun-dyed viscose fibers [J]. Journal of Textile Research, 2020, 41(07): 9-14.
[6] LI Liping, WU Daoyi, ZHAN Yikai, HE Min. Review on carbon fiber surface modification using electrophoretic deposition of carbon nanotubes and graphene oxide [J]. Journal of Textile Research, 2020, 41(06): 168-173.
[7] WANG Zongqian, YANG Haiwei, ZHOU Jian, LI Changlong. Effect of urea degumming on mechanical properties of silk fibroin aerogels [J]. Journal of Textile Research, 2020, 41(04): 9-14.
[8] DING Fang, REN Xuehong. Flame-retardant finishing of polyester fabrics by grafting phosphorus-nitrogen compounds [J]. Journal of Textile Research, 2020, 41(03): 100-105.
[9] CUI Yifan, HOU Wei, ZHOU Qianxi, YAN Jun, LU Yanhua, HE Tingting. Influence of silk sericin temperature sensitive hydrogel on properties of cotton fabrics [J]. Journal of Textile Research, 2019, 40(12): 74-78.
[10] ZHANG Jiao, GAO Xuefeng, WANG Yuzhou, LIU Haihui, ZHANG Xingxiang. Preparation and properties of polyamide 66/amino-functionalized multi-walled carbon nanotubes fibers [J]. Journal of Textile Research, 2019, 40(11): 1-8.
[11] YANG Fan, LIU Junhua, BIAN Angting, WANG Yanping, QIAN Qiyuan, NI Jianhua, XIA Yumin, HE Yong, WANG Yimin. Influence of heat treatment on structure and properties of thermotropic liquid crystalline polyarylate fiber [J]. Journal of Textile Research, 2019, 40(11): 9-12.
[12] XIAO Chuanmin, XIAO Changfa, ZHANG Tai, WANG Xinya. Structure and properties of braided tube reinforced polylactic acid hollow fiber membranes [J]. Journal of Textile Research, 2019, 40(08): 20-26.
[13] WU Liwei, WANG Wei, LIN Jiahorng, JIANG Qian. Preparation and mechanical properties of aramid/ ultra-high molecular weight polyethylene fabric reinforced polyurethane sandwich composite [J]. Journal of Textile Research, 2019, 40(07): 64-70.
[14] LIU Shuping, LI Liang, LIU Rangtong, CUI Shizhong, WANG Yanting. Structure and properties of keratin film modified by carboxymethyl cellulose sodium [J]. Journal of Textile Research, 2019, 40(06): 14-19.
[15] LIU Jinxin, ZHANG Haifeng, ZHANG Xing, HUANG Chen, ZHENG Xiaobing, JIN Xiangyu. Influence of multistage drawing and heat setting on structure and properties of polyethylene/polypropylene bicomponent fibers [J]. Journal of Textile Research, 2019, 40(05): 24-29.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd