Journal of Textile Research ›› 2019, Vol. 40 ›› Issue (10): 68-72.doi: 10.13475/j.fzxb.20180200505

• Textile Engineering • Previous Articles     Next Articles

Current response in stretching process of Cu-Ni metal-coated woven fabric

JIA Gaopeng1(), SONG Xiaohong2, LI Ying3, LIU Xiaodan4, PAN Xueru1   

  1. 1. College of Textile & Clothing, Yancheng Institute of Technology, Yancheng, Jiangsu 224051, China;
    2. Jiangxi Fiber Inspection Bureau, Nanchang, Jiangxi 330029, China
    3. Shaanxi Textile Science Institute,Xi'an, Shaanxi 710038, China
    4. Henan Fiber Inspection Bureau, Zhengzhou, Henan 450008, China
  • Received:2018-02-01 Revised:2019-01-23 Online:2019-10-15 Published:2019-10-23

RichHTML

2

PDF (PC)

79

Abstract:

In order to investigate the sensing performance of metal-coated woven fabric as soft sensor, the current variation of the fabric to tension at different tensile speeds was experimentally investigated by means of a fabric tension machine and a self-made current acquisition system. The rule of current response to tension was discussed. The influence of different tensile speeds on the current response and the difference between sensitivity in warp and weft direction was analyzed. The results show that the current response of polyester-based metal-coated woven fabric to the tensile in the warp and weft direction shows high linearity at higher tensile speeds, the current response to the low-speed tensile shows more worse linearity compared with that to higher-speed tensile, and the sensitivity of the fabric to tensile in warp and weft directions will decrease with the tensile speed increase. The fabric shows the better elongation at break in the weft direction than that in the warp direction, the current response in the weft direction shows the higher sensitivity than that in the warp direction, and larger sensitivities exist in low speed stretching process.

Key words: metal-coated woven fabric, soft sensor, polyester, current response, sensitivity

CLC Number: 

  • TS101.8

Fig.1

Schematic of current response in process of fabric stretching"

Fig.2

Setup of testing device of current response in stretching process"

Fig.3

Current response in warp direction to tensile process"

Fig.4

Morphological photo of fabric breaking position"

Fig.5

Current response in weft direction to tensile process"

Tab.1

Sensitivity and strain in warp and weft direction"

拉伸速度/
(mm·min-1)		 经向 纬向
ε G ε G
20 0.16 1.36 0.22 8.67
100 0.15 2.30 0.20 2.90
200 0.14 0.94 0.18 1.67
300 0.13 0.90 0.16 0.72
[1] 杨斌, 陶肖明, 俞建勇. 不锈钢纤维织物的电阻与应变关系[J]. 稀有金属材料与工程, 2006,35(1):96-99.
YANG Bin, TAO Xiaoming, YU Jianyong. A study on the relation between resistance and strain based on stainless steel fabric[J]. Rare Metal Materials and Engineering, 2006,35(1):96-99.
[2] 张辉. 本征导电纤维集合体的电-力学性能及其作为应变、压力传感器的性能分析[D]. 上海:东华大学, 2006.
ZHANG Hui. Electromechanical properties of intrinsically conductive fiber assembles, its textile structure and applications as strain and pressure sensors[D]. Shanghai: Donghu University, 2006.
[3] ZHANG Hui, TAO Xiaoming, YU Tongxi, et al. Conductive knitted fabric as large-strain gauge under high temperature[J]. Sensors and Actuators, 2016,126:129-140.
[4] 王金凤, 龙海如. 基于导电纤维针织物的柔性传感器研究[J]. 纺织导报, 2011(5):76-80.
WANG Jinfeng, LONG Hairu. Research on flexible sensors based on knitted fabric with conductive fiber[J]. China Textile Leader, 2011(5):76-80.
[5] 王金凤, 龙海如. 线圈转移对导电弹性针织物柔性传感器的电-力学性能影响[J]. 纺织学报, 2013,34(7):62-68.
WANG Jinfeng, LONG Hairu. Effect of loop transfer on electro-mechanical properties of conductive elastic wearable knitted sensors[J]. Journal of Textile Research, 2013,34(7):62-68.
[6] 张舒, 缪旭红. 经编导电针织物的应变-电阻传感能[J]. 纺织学报, 2018,39(2):73-77.
ZHANG Shu, MIAO Xuhong. Strain resistance sensing property of the warp knitted conductive fabric[J]. Journal of Textile Research, 2018,39(2):73-77.
[7] 蔡倩文, 王金凤, 陈慰来. 纬编针织柔性传感器结构及其导电性能[J]. 纺织学报, 2016,37(6):31-35.
CAI Qianwen, WANG Jinfeng, CHEN Weilai. Structures and electrical properties of weft-knitted flexible sensors[J]. Journal of Textile Research, 2016,37(6):31-35.
[8] 刘焘, 邹奉元. 涂碳纤维导电针织物的结构设计及其传感性能[J]. 纺织学报, 2014,35(9):31-35.
LIU Tao, ZOU Fengyuan. Structural design and sensing performance of conductive knitted fabrics of carbon coated fibers[J]. Journal of Textile Research, 2014,35(9):31-35.
[9] 洪剑寒, 潘志娟, 姚穆. 超高分子量聚乙烯/聚苯胺导电针织物的应变传感性能[J]. 纺织学报, 2016,37(2):73-78.
HONG Jianhan, PAN Zhijuan, YAO Mu. Strain sensing property of knitted fabric of conductive ultrahigh molecular weight polyethylene/polyaniline composite yarn[J]. Journal of Textile Research, 2016,37(6):73-78.
[10] 李选. 导电纤维纺织结构温度/应变传感性能的研究[D]. 杭州: 浙江理工大学, 2011: 10-36.
LI Xuan. A study on the sensitivity of conducting fiber temperature/strain sensing based on textile structure [D]. Hongzhou: Zhejiang Sci-Tech University, 2011: 10-36.
[1] WANG Qiuping, ZHANG Ruiping, LI Chenghong, ZHANG Gecheng. Preparation and characterization of conductive polyester nonwovens [J]. Journal of Textile Research, 2020, 41(10): 116-121.
[2] CHEN Yong, WANG Jingjing, WANG Chaosheng, GU Donghua, WU Jing, WANG Huaping. Effect of oligomers on crystalline properties of polytrimethylene terephthalate [J]. Journal of Textile Research, 2020, 41(10): 1-6.
[3] LI Liang, LIU Jingfang, HU Zedong, GENG Changjun, LIU Rangtong. Graphene oxide loading on polyester fabrics and antistatic properties [J]. Journal of Textile Research, 2020, 41(09): 102-107.
[4] DUO Yongchao, QIAN Xiaoming, ZHAO Baobao, QIAN Yao, ZOU Zhiwei. Preparation and properties of microfiber synthetic leather base [J]. Journal of Textile Research, 2020, 41(09): 81-87.
[5] ZHANG Lingyun, QIAN Xiaoming, ZOU Chi, ZOU Zhiwei. Preparation and properties of SiO2 aerogel / polyester-polyethylene bicomponent fiber composite thermal insulation materials [J]. Journal of Textile Research, 2020, 41(08): 22-26.
[6] ZHANG Zhuhui, ZHANG Diantang, QIAN Kun, XU Yang, LU Jian. Weaving process and off-axial tensile mechanical properties of wide-angle woven fabric [J]. Journal of Textile Research, 2020, 41(08): 27-31.
[7] CHEN Wendou, ZHANG Hui, CHEN Tianyu, WU Hailiang. Self-cleaning properties of titanium dioxide modified polyester / cotton blend fabrics [J]. Journal of Textile Research, 2020, 41(07): 122-128.
[8] LIU Guojin, HAN Pengshuai, CHAI Liqin, WU Yu, LI Hui, GAO Yafang, ZHOU Lan. Preparation and stability of self-crosslinking P(St-NMA) photonic crystals with structural colors on polyester fabrics [J]. Journal of Textile Research, 2020, 41(05): 99-104.
[9] JI Hong, ZHANG Yang, CHEN Kang, SONG Minggen, JIANG Quan, FAN Yonggui, ZHANG Yumei, WANG Huaping. Developing black high-tenacity polyester yarns based on dynamic characteristics [J]. Journal of Textile Research, 2020, 41(04): 1-8.
[10] WANG Xiaofei, WAN Ailan. Preparation of polypyrrole / silver conductive polyester fabric by ultraviolet exposure [J]. Journal of Textile Research, 2020, 41(04): 112-116.
[11] LIN Jiameng, WAN Ailan, MIAO Xuhong. Preparation and properties of polypyrrole / silver conductive polyester fabrics [J]. Journal of Textile Research, 2020, 41(03): 113-117.
[12] DING Fang, REN Xuehong. Flame-retardant finishing of polyester fabrics by grafting phosphorus-nitrogen compounds [J]. Journal of Textile Research, 2020, 41(03): 100-105.
[13] XING Dandan, WANG Ni, LIU Huyi, GAN Xuehui, SHI Meiwu. Characterization on distribution of TiO2 particles in opaque polyester and dull nylon filaments [J]. Journal of Textile Research, 2020, 41(02): 33-38.
[14] ZHEN Qi, ZHANG Heng, ZHU Feichao, SHI Jianhong, LIU Yong, ZHANG Yifeng. Fabrication and properties of polypropylene / polyester bicomponent micro-nanofiber webs via melt blowing process [J]. Journal of Textile Research, 2020, 41(02): 26-32.
[15] LI Sijie, ZHANG Caidan. Preparation of poly(aspartic acid) based fiber hydrogel and its drug release behavior [J]. Journal of Textile Research, 2020, 41(02): 20-25.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd