纺织学报 ›› 2018, Vol. 39 ›› Issue (04): 14-18.doi: 10.13475/j.fzxb.20170503805

• 纤维材料 • 上一篇    下一篇

沉积静电纺聚丙烯腈纳米纤维膜窗纱的制备及其性能

  

  • 收稿日期:2017-05-22 修回日期:2018-01-11 出版日期:2018-04-15 发布日期:2018-04-20

Preparation and properties of electrospun polyacrylonitrile nanofiber coated window screen

  • Received:2017-05-22 Revised:2018-01-11 Online:2018-04-15 Published:2018-04-20

摘要:

为提升室内空气质量,采用纳米静电纺丝技术,在传统的玻璃纤维窗纱上沉积聚丙烯腈(PAN)纳米纤维膜,制备具有防PM2.5 作用的窗纱。探讨了PAN纺丝液质量分数、窗纱基材对纤维微观形貌的影响,考察了窗纱的透光性、透气性和防PM2.5效果。结果表明:PAN纺丝液质量分数为10%,电压为20 kV,时间为0.5 h条件下,制备的纤维直径分布均匀,平均直径约为225 nm;PAN 纳米纤维膜在窗纱纱棱处沉积较厚,而在窗纱空隙处沉积较薄,这种结构增加了纳米纤维膜与窗纱的连接力;PAN纳米纤维膜使窗纱透光率下降12%,透气率下降35%;随着过滤测试时间的增加,PM 2.5吸附效果显著,窗纱表面吸附物中含有机官能团,室内空气质量变好;测试2 h后,对PM 2.5的截留率达到63%,窗纱的透光性、透气性随PM2.5吸附程度的增加而下降。

关键词: 聚丙烯腈纳米纤维, 空气过滤, 防PM2.5窗纱, 静电纺丝

Abstract:

In order to improve the indoor air puality, polypropylene (PAN) nanofibers were coated on conventional glass-fiber screen by electrospinning to prepare anti PM 2.5  window screen. The influence of spinning solution concentration and base material of the window screen on the microstructure of the electrospun nanofibers were studied, and the anti PM 2.5 effect, transparent and air permeability of the window screen were also investigated. The results show that when the concentration of PAN spinning solution is 10 %, the voltage is 20 kV and the time is 0.5 h, the well-distributed nanofibers with mean diameters of 170 nm can be formed. On the window screen surface, the PAN films are deposited on the warp and weft yarn with a thickness greater than those deposited on the gap of the window screen. This structure improved the connected force of the nanofiber film with the window screen and the permeability of the window screen. However, the transparency of the wondow screen decreases by 12% and air permeability decreases by 35% due to the deposition of PAN nanofibers. With the increasing of PM2.5 testing time, the adsorption effect is increased. Some organic functional groups are adsorbed on the screen surface. Then the indoor air quality became better. After 2 h testing, the rejection ratio of PM2.5 reaches 63%. With the increasing of PM2.5 adsorption, the transparency and air permeability of the window screendecrease correspondingly.

Key words: polyacrylonitrile nanofiber, air filtering, anti PM2.5 window screen, electrospinning

[1] 吴小娟 余妙晶 舒慧 郑怡筱 葛烨倩 . 过温保护层合纳米纤维隔膜的制备及其性能[J]. 纺织学报, 2018, 39(07): 21-26.
[2] 朱金铭 钱建华 曹晨 曹原. 聚醚砜非织造布复合膜的空气过滤性能[J]. 纺织学报, 2018, 39(07): 55-62.
[3] 陈洪立 焦晓宁 柯鹏. 取向增强复合锂离子电池隔膜的制备及其性能[J]. 纺织学报, 2018, 39(07): 8-14.
[4] 张博亚 李佳慧 张如全 李建强. 静电纺聚丙烯腈/硫酸铜纳米纤维膜的制备及其性能[J]. 纺织学报, 2018, 39(07): 15-20.
[5] 王航 庄旭品 董锋 石磊 康卫民 徐先林 程博闻. 溶液喷射纺纳米纤维制备技术及其应用进展[J]. 纺织学报, 2018, 39(07): 165-173.
[6] 靳世鑫 辛斌杰 郑元生. 静电纺丝法宏量制备纳米纤维的研究进展[J]. 纺织学报, 2018, 39(03): 175-180.
[7] 刘雷艮 林振锋 沈忠安 牛建涛. 静电纺多孔超细纤维膜的吸油性能[J]. 纺织学报, 2018, 39(02): 7-13.
[8] 蒋洁 陈胜 李静静 付润芳 林义 顾迎春. 静电纺钛酸钡/聚偏氟乙烯纳米复合柔性压电纤维膜[J]. 纺织学报, 2018, 39(02): 14-19.
[9] 李静静 卢辉 蒋洁 张思航 顾迎春 陈胜. 高压电性静电纺柔性氧化锌/聚偏氟乙烯复合纤维膜[J]. 纺织学报, 2018, 39(02): 1-6.
[10] 王永鹏 刘梦竹 路大勇. 用静电纺丝法制备可交联高性能聚合物纳米纤维[J]. 纺织学报, 2018, 39(01): 6-10.
[11] 李树锋 刘高华 谢小军 韩永兴 张艳 程博闻. 同轴静电纺丝参数对聚丙烯腈中空碳纳米纤维形态与炭化收率的影响[J]. 纺织学报, 2017, 38(12): 1-6.
[12] 康卫民 范兰兰 邓南平 何宏升 鞠敬鸽 程博闻 . 静电纺多孔碳纳米纤维制备与应用研究进展[J]. 纺织学报, 2017, 38(11): 168-176.
[13] 李智勇 邵一卿 孙窈 张亮 夏鑫. 含氟聚氨酯的合成及其静电纺膜复合织物的防酸透湿性能[J]. 纺织学报, 2017, 38(10): 7-12.
[14] 王闻宇 朱承章 张琼之 金欣 肖长发 林童 朱正涛. 二甲基亚砜/水溶液体系中氢键对静电纺淀粉纤维的影响[J]. 纺织学报, 2017, 38(09): 19-23.
[15] 陈锋 姬忠礼 齐强强. 静电纺聚丙烯腈纳米纤维复合滤材的制备及其气液过滤性能[J]. 纺织学报, 2017, 38(09): 8-13.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!