阳离子染料常压可染新型改性涤纶的热性能及染色性能

  

  • 收稿日期:2016-01-26 修回日期:2016-09-02 出版日期:2016-12-15 发布日期:2016-12-21

Thermal and dyeing properties of novel cationic-dyeable polyester fabrics under atmospheric pressure

  • Received:2016-01-26 Revised:2016-09-02 Online:2016-12-15 Published:2016-12-21

摘要:

针对常规涤纶常压难以上染的问题,对一种新型改性涤纶的热性能和染色性能进行研究。使用扫描电子显微镜、差示扫描量热法和热失重分析等对纤维形貌及热性能进行表征和测试。结果表明:纤维具有纵向沟槽及横向十字形结构;玻璃化转变温度为62℃,结晶温度为131℃,熔点为241℃,初始热分解温度为402.8 ℃。利用亚甲基蓝上染纤维,测得纤维的染色饱和值为5.8。使用Maxilon 阳离子染料(红、金黄、蓝、黑)对织物进行染色并绘制上染速率曲线,结果表明:入染30 min后可达到染色平衡,染色保温时间为30min,染色样品色牢度均能达到4级左右;黑色染料用量为5%(o.w.f )时,K/S值变化趋于平缓,干湿摩擦牢度为4∽5 级。

关键词: 阳离子染料, 改性涤纶, 染色性能, 色牢度

Abstract:

In view of the proboem of the conventional polyester fiber on the difficulty dyeing fiber under atmospheric pressure, the thermal and dyeing properties of a novel modified polyester fiber were studied. The morphology and thermal properties of the fibers were characterized and tested by scanning electron microscope, differential scanning calorimetry and thermal gravimetric analysis. The results show that the fiber has longitudinal grooves and cross-shaped structures; the glass transition temperature, crystallization temperature, melting point and initial thermal decomposition temperature of fibres are 62 ℃, 131 and 241 ℃, respectively. The dyeing saturation value of fiber was measured by using methylene blue dye on the fiber, and the dyeing saturation value is 5.8. The fabrics are dyed with Maxilon cationic dyes(red,golden yellow,blue and black), and the dyeing rate curves are drawn. The results show that the dyeing balance can be reached after 30min, the holding time is 30 min and the color fastness is about 4 grade. The fabric is dyed with Maxilon Black, and the results show that the K/S value tends to be stable when the dye concentration is about 5 %(o.w.f.), and the dry and wet rubbing fastness is 4~5 grade.

Key words: cationec dye, modified polyester, dyeing performance, color fastness

[1] 梁静 钟毅 毛志平 徐红 张琳萍 隋晓锋. 晶型对分散染料染色性能的影响[J]. 纺织学报, 2018, 39(07): 69-73.
[2] 舒大武 房宽峻 刘秀明 刘曰兴 蔡玉青 门雅静 李付杰. 活性染料无盐连续轧-蒸与冷轧堆染色效果的比较[J]. 纺织学报, 2018, 39(04): 77-81.
[3] 姚萍 江文 王江 黄金洪 周小华. 接枝壳寡糖抗菌粘胶纤维的制备及其抗菌性与染色效果[J]. 纺织学报, 2018, 39(04): 9-13.
[4] 刘艳春 白刚 钱红飞. 聚酰亚胺织物的羧基化表面改性[J]. 纺织学报, 2018, 39(03): 103-107.
[5] 俞俭 王业师 吕景春 周天池 魏取福. 低温等离子体处理木棉纤维的染色性能[J]. 纺织学报, 2017, 38(12): 88-94.
[6] 张婉 籍晓倩 殷允杰 王潮霞. 用溶胶微球法制备变色涤纶织物的温致变色机制及其性能[J]. 纺织学报, 2017, 38(02): 117-122.
[7] 陈思 邱夷平 施楣梧 蒋秋冉. 用于天然纤维素纤维纱线的无浆料浆纱技术[J]. 纺织学报, 2016, 37(2): 85-0.
[8] 盛杰侦 闫新 秦俊霞 曹机良. 不对称咪唑类离子液体对腈纶缓染性能的影响[J]. 纺织学报, 2016, 37(10): 68-72.
[9] 丁彩玲 俞建勇 张瑞云 李慧 程隆棣 秦光. 超细羊毛的低温低损伤染色性能[J]. 纺织学报, 2016, 37(06): 72-75.
[10] 林琳 于俊荣 陈蕾 王彦 诸静 胡祖明. 未干聚对苯二甲酰对苯二胺纤维的染色工艺[J]. 纺织学报, 2015, 36(08): 84-88.
[11] 王维明 虞波 陈缘晴 王中正. 改性聚酯纤维用防活性染料沾色剂的制备及其适用性[J]. 纺织学报, 2015, 36(06): 72-0.
[12] 丁川 张建春 冯新星 刘雪强 来侃. 电子束辐照对涤纶染色性能的影响[J]. 纺织学报, 2014, 35(7): 79-0.
[13] 刘剑 陈克 周旸 赵丰 彭志勤 胡智文. 微型光纤光谱技术在植物染料鉴别与光照色牢度评估中的应用[J]. 纺织学报, 2014, 35(6): 85-0.
[14] 黄玉华 罗艳辉 蒲宗耀 吴晋川 胡于庆. 涂料印花织物的耐摩擦色牢度评定[J]. 纺织学报, 2013, 34(7): 90-94.
[15] 王秀华 沈金科 沈国光 李为民 李邵波 周翔 姚玉元. 一步法PET/CDP混纤牵伸丝的制备与性能[J]. 纺织学报, 2013, 34(5): 30-34.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!