Journal of Textile Research ›› 2019, Vol. 40 ›› Issue (10): 13-19.doi: 10.13475/j.fzxb.20181000607

• Fiber Materials • Previous Articles     Next Articles

Kinetics and properties of phosphorus flame retardant copolymerized polyester

CHEN Yong1, WANG Ying1, HE Feng1, WANG Jing1, ZHU Zhiguo1(), DONG Zhenfeng1, WANG Rui1,2   

  1. 1. School of Materials Science and Engineering, Beijing Institute of Fashion Technology, Beijing 100029, China
    2. Beijing Key Laboratory of Clothing Materials R&D and Assessment, Beijing 100029, China;
  • Received:2018-10-09 Revised:2019-07-05 Online:2019-10-15 Published:2019-10-23
  • Contact: ZHU Zhiguo E-mail:clyzzg@bift.edu.cn

RichHTML

4

PDF (PC)

152

Abstract:

In order to investigate the reaction law and influencing factors of copolymerized phosphorus-based flame retardant polyesters(PET), flame retardant co-PETs was prepared by using 2-carboxyethyl phenyl phosphinic acid (CEPPA) as a co-monomer flame retardant. The kinetic model of the polycondensation reaction of PET and flame retardant co-PETs were established, and the trend and reasons of the kinetic model were analyzed. The structure and properties of polymer were characterized by infrared spectroscopy, differential scanning calorimetry, thermogravimetry, limiting oxygen index and cone calorimetry. The results show that with the increase of the mass fraction of CEPPA, the actiration energy of reaction increases to 106.83 kJ/mol. The glass transition temperature and melting point decreases with the increase of the flame retardant because the group structure of CEPPA is polymerized into the macromolecular chain, which inhibits the crystallization of the PET. PET with the phosphorus content of 1% can achieve the optimal flame retardancy, limit oxygen index can be up to 31%, the ignition time is prolonged obviously, and the peak heat release rate decreases by 24%.

Key words: polyester, kinetics model of polycondensation, flame retardant, phosphorus-containing flame retardant polyester

CLC Number: 

  • TQ311

Fig.1

Change of molecular weight of flame retardant PET of different padditions with time"

Tab.1

Linear regression equations for PET with different padditions"

磷质量
分数/%		 聚合温
度/℃		 回归方程 R2
0.0 275 Mt=203.18t+746.5 0.99
280 Mt=230.90t+1 598.0 0.99
285 Mt=252.49t+1 485.0 0.99
0.6 275 Mt=179.70t+1 411.6 0.97
280 Mt=206.85t+1 178.1 0.97
285 Mt=235.75t+2 376.8 0.96
0.8 275 Mt=157.17t+816.2 0.98
280 Mt=199.14t+366.8 0.96
285 Mt=229.54t+1 501.1 0.97
1.0 275 Mt=138.86t+254.6 0.98
280 Mt=185.91t+691.6 0.98
285 Mt=211.23t+693.3 0.98

Tab.2

Effect of polymerization temperature on apparent reaction rate constant of different systems"

磷质量分
数/%		 K/(g·(mol·min)-1)
275 ℃ 280 ℃ 285 ℃
0.0 203.18 230.90 252.49
0.6 179.70 206.85 235.75
0.8 157.17 199.14 229.54
1.0 138.86 185.91 211.23

Tab.3

Result of activation energies and pre-exponential factors for different polymerization systems"

磷质量分
数/%		 lnK与T-1方程 Ea/
(kJ·mol-1)		 A0/
(g·(mol·min)-1)
0.0 lnK=-6 651T-1 + 17.45 55.30 3.80×107
0.6 lnK=-8 307T-1 + 20.35 69.06 6.86×108
0.8 lnK=-11 596T-1 + 26.23 96.41 2.46×1011
1.0 lnK=-12 849T-1 + 28.40 106.83 2.16×1012

Fig.2

Infrared spectra of PET and flame retardant PET"

Fig.3

DSC spectra of PET and flame retardant PET"

Tab.4

TGA data for PET and flame retardant PET"

样品
编号		 初始分解
温度/℃		 最大分解速
率温度/℃		 最终残
碳量/%
1# 397.7 431.6 22.5
2# 396.0 429.9 21.0
3# 395.0 428.8 20.7
4# 389.9 430.7 21.2
5# 387.3 430.9 17.8
6# 387.1 432.1 16.6
7# 390.0 429.9 22.3
8# 389.2 430.1 23.9
9# 382.9 429.7 17.4
10# 384.1 430.9 19.3
11# 383.7 429.6 18.5
12# 382.8 428.7 18.7

Fig.4

Cone calorimetry test curve of sample. (a)Curve of heat release rate; (b)Curve of total heat release"

[1] 王新良. 阻燃聚酯现状及发展趋势[J]. 聚酯工业, 2012,25(5):5-7.
WANG Xinliang. Current status and development trends of flame-retardant polyester[J]. Polyester Industry, 2012,25(5):5-7.
[2] 李建武, 王朝生, 江振林, 等. 含磷阻燃剂结构对阻燃共聚酯结构与性能的影响[J]. 合成纤维工业, 2017,40(3):6-10.
LI Jianwu, WANG Chaosheng, JIANG Zhenlin, et al. Structure and properties of flame retardant copolyester dependent on phosphorous flame retardant structure[J]. China Synthetic Fiber Industry, 2017,40(3):6-10.
[3] 闫梦祥, 张思源, 王总帅, 等. 磷系阻燃剂阻燃PET的研究进展[J]. 中国塑料, 2017,31(10):1-5.
YAN Mengxiang, ZHANG Siyuan, WANG Zongshuai, et al. Research progress in phosphorus flame retardants for polyesters[J]. China Plastics, 2017,31(10):1-5.
[4] 黄基锐, 沙建昂, 龚静华, 等. 高磷含量阻燃聚酯及其与聚对苯二甲酸乙二醇酯共混物的制备研究[J]. 化工新材料, 2017,45(12):122-125.
HUANG Jirui, SHA Jian'ang, GONG Jinghua, et al. Preparation of flame retardant polyester with hige phosphorus content and its blend with PET[J]. New Chemical Meterials, 2017,45(12):122-125.
[5] 韩永刚. 磷系阻燃聚酯的制备及性能研究[D]. 长春:长春工业大学, 2017: 25-43.
HAN Yonggang. Study on the preparation and properties of phosphorus-containing flame retardant polyester[D]. Changchun: Changchun University of Technology, 2017: 25-43.
[6] 孙晓凯. 含磷阻燃聚酯纳米复合物的制备及其结构性能研究[D]. 北京:北京服装学院, 2009: 25-40.
SUN Xiaokai. Studies on synthesis of flame-retardant ploy(ethylene terephthalate)/nanocomposites and its properties[D]. Beijing: Beijing Institute of Fashion Technology, 2009: 25-40.
[7] 王国德, 王红, 赵清刚. 阻燃剂2-羧乙基苯磷酸在阻燃聚酯中的应用[J]. 聚酯工业, 2002,15(4):18-19.
WANG Guode, WANG Hong, ZHAO Qingang. Application of 2-carboxyethyl (phenyl)phosphinic acid as phosphorus- containing flame-retardant on PET[J]. Polyester Industry, 2002,15(4):18-19.
[8] 冯新星, 张建春, 张华, 等. 含磷阻燃共聚聚酯的制备及性能[N]. 中国纺织报, 2013-09-02(4).
FENG Xinxing, ZHANG Jianchun, ZHANG Hua, et al. Preparation and properties of phosphorus-containing flame retardant copolyester[N]. China Textile News, 2013-09-02(4).
[9] 姬洪. 阻燃涤纶的制备、结构与性能研究[D]. 杭州:浙江理工大学, 2012: 5-43.
JI Hong. Preparation, structure and properties of flame-retardant polyester fiber[D]. Hangzhou: Zhejiang Sci-Tech University, 2012: 5-43.
[10] 张宁. 功能性聚酯的制备与性能[D]. 武汉:武汉工程大学, 2016: 13-47.
ZHANG Ning. Preparation and properties of functional polyester[D]. Wuhan:Wuhan Institute of Technology, 2016: 13-47.
[11] 陈克权, 周芬, 陈尚伟, 等. Ti/Si系催化剂催化聚酯缩聚反应动力学研究[J]. 聚酯工业, 2002,15(4):15-17.
CHEN Kequan, ZHOU Fen, CHEN Shangwei, et al. Study on the reaction kinetics of Ti/Si catalyst for PET polycondensation[J]. Polyester Industry, 2002,15(4):15-17.
[12] 李文艳, 顾雪萍, 王嘉骏, 等. 规模化聚对苯二甲酸乙二醇酯终缩聚的流程模拟[J]. 石油化工, 2011,40(10):1094-1099.
LI Wenyan, GU Xueping, WANG Jiajun, et al. Modeling of an industrial polycondensation process for polyethylene terephthalate[J]. Petrochemical Technology, 2011,40(10):1094-1099.
[13] 武荣瑞, 张天骄. 成纤聚合物的合成与改性[M]. 北京: 中国石化出版社, 2002: 75-93.
WU Rongrui, ZHANG Tianjiao. Synthesis and Modification of Fiber-forming Polymers[M]. Beijing: China Petrochemical Press, 2002: 75-93.
[14] 刘方, 刘亮, 李璐, 等. 对苯二甲酸与新戊二醇缩聚反应动力学研究[J]. 化学研究与应用, 2016,28(9):1320-1324.
LIU Fang, LIU Liang, LI Lu, et al. Kinetics of polycondensation interephthalic acid and neopentyl glycol reaction[J]. Chemical Research and Application, 2016,28(9):1320-1324.
[15] 缪飞. 磷硅阻燃剂的合成与表征及在环氧树脂中的应用[D]. 绵阳:西南科技大学, 2018: 3-16.
MIAO Fei. Synthesis and characterization of phosphorus-silicon flame retardant and its application in epoxy resin[D]. Mianyang: Southwest University of Science and Technology, 2018: 3-16.
[16] 江振林. 聚酯纤维及织物的阻燃与抗熔滴改性[D]. 上海:东华大学, 2018: 31-53.
JIANG Zhenlin. Flame retardant and anti-dropping modification of polyester fiber and fabric[D]. Shanghai:Donghua University, 2018: 31-53.
[1] WANG Qiuping, ZHANG Ruiping, LI Chenghong, ZHANG Gecheng. Preparation and characterization of conductive polyester nonwovens [J]. Journal of Textile Research, 2020, 41(10): 116-121.
[2] WANG Yang, CHENG Chunzu, JIANG Li′na, REN Yuanlin, GUO Yingbin. Preparation of durable flame retardant polyacrylonitrile fabrics using UV-induced photo-grafting polymerization combined with sol-gel coating [J]. Journal of Textile Research, 2020, 41(10): 107-115.
[3] CHEN Yong, WANG Jingjing, WANG Chaosheng, GU Donghua, WU Jing, WANG Huaping. Effect of oligomers on crystalline properties of polytrimethylene terephthalate [J]. Journal of Textile Research, 2020, 41(10): 1-6.
[4] LI Liang, LIU Jingfang, HU Zedong, GENG Changjun, LIU Rangtong. Graphene oxide loading on polyester fabrics and antistatic properties [J]. Journal of Textile Research, 2020, 41(09): 102-107.
[5] DUO Yongchao, QIAN Xiaoming, ZHAO Baobao, QIAN Yao, ZOU Zhiwei. Preparation and properties of microfiber synthetic leather base [J]. Journal of Textile Research, 2020, 41(09): 81-87.
[6] ZHANG Lingyun, QIAN Xiaoming, ZOU Chi, ZOU Zhiwei. Preparation and properties of SiO2 aerogel / polyester-polyethylene bicomponent fiber composite thermal insulation materials [J]. Journal of Textile Research, 2020, 41(08): 22-26.
[7] ZHANG Zhuhui, ZHANG Diantang, QIAN Kun, XU Yang, LU Jian. Weaving process and off-axial tensile mechanical properties of wide-angle woven fabric [J]. Journal of Textile Research, 2020, 41(08): 27-31.
[8] CHEN Wendou, ZHANG Hui, CHEN Tianyu, WU Hailiang. Self-cleaning properties of titanium dioxide modified polyester / cotton blend fabrics [J]. Journal of Textile Research, 2020, 41(07): 122-128.
[9] ZHOU Qingqing, CHEN Jiayi, QI Zhenming, CHEN Weijian, SHAO Jianzhong. Preparation and characterization of flame retardant and antibacterial cotton fabric [J]. Journal of Textile Research, 2020, 41(05): 112-120.
[10] LIU Guojin, HAN Pengshuai, CHAI Liqin, WU Yu, LI Hui, GAO Yafang, ZHOU Lan. Preparation and stability of self-crosslinking P(St-NMA) photonic crystals with structural colors on polyester fabrics [J]. Journal of Textile Research, 2020, 41(05): 99-104.
[11] JI Hong, ZHANG Yang, CHEN Kang, SONG Minggen, JIANG Quan, FAN Yonggui, ZHANG Yumei, WANG Huaping. Developing black high-tenacity polyester yarns based on dynamic characteristics [J]. Journal of Textile Research, 2020, 41(04): 1-8.
[12] WANG Xiaofei, WAN Ailan. Preparation of polypyrrole / silver conductive polyester fabric by ultraviolet exposure [J]. Journal of Textile Research, 2020, 41(04): 112-116.
[13] GAO Shan, LU Yehu, ZHANG Desuo, WU Lei, WANG Laili. Thermal protective performance of composite flame retardant fabrics treated by graphene aerogel [J]. Journal of Textile Research, 2020, 41(04): 117-122.
[14] LIN Jiameng, WAN Ailan, MIAO Xuhong. Preparation and properties of polypyrrole / silver conductive polyester fabrics [J]. Journal of Textile Research, 2020, 41(03): 113-117.
[15] DING Fang, REN Xuehong. Flame-retardant finishing of polyester fabrics by grafting phosphorus-nitrogen compounds [J]. Journal of Textile Research, 2020, 41(03): 100-105.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd