Preparation and properties of flexible flame retardant polyamide coated fabric via wet coating

CHEN Zhijie1(), YU Yihao2, FU Ye2, LEI Pengfei2, JIANG Jikang3, QI Dongming3   

  1. 1. Key Laboratory of Surface Modification of Polymer Materials and Mechanical and Electrical Products, Wenzhou Polytechnic, Wenzhou, Zhejiang 325035, China
    2. Zhejiang King Label Technology Co., Ltd., Huzhou, Zhejiang 313100, China
    3. Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou, Zhejiang 310018, China
  • Received:2020-11-27 Revised:2021-05-17 Online:2021-11-15 Published:2021-11-29

RichHTML

13

PDF (PC)

85

Abstract:

In order to address the poor performance of polyamide coated fabric's hand feel and flame retardant properties, caused by insoluble particulate flame retardant, the research introduced 9,10-dihydrogen-9-oxygen hybrid-10-phosphorus hexafil-10-oxide (DOPO) into the polyamide/methanol-calcium chloride solution. A porous, light and thin polyamide coating with DOPO uniformly dispersed, and a smooth and flat surface coating on the fabric were created on the fabric via wet coating which including coating, water exchange into film and drying process. The effects of DOPO and particulate flame retardants on the fluid properties of the polyamide/methanol-calcium chloride solution system were investigated and compared. The results show that DOPO changes the rheological properties of the solution, but does not significantly increase the shear viscosity of the system, which is beneficial to coating processing. According to the test of flame retardant properties and stiffness, it was found that DOPO can effectively improve the flame retardant properties of the coated fabric and retain the flexibility of the fabric compared to the flame retardant particles.

Key words: 9,10-dihydrogen-9-oxygen hybrid-10-phosphorus hexafil-10-oxide, polyamide coating, flame retardant textiles, wet coating, flexible fabric

CLC Number: 

  • TQ325

Fig.1

Effect of DOPO and MCA content on shear viscosity and particle size of polyamide/methanol-calcium chloride slurry coating"

Fig.2

Shear rate and shear viscosity of original and DOPO、MCA polyamide/methanol-calcium chloride slurry coating"

Fig.3

SEM images of polyamide coating containing DOPO and MCA (×2 000)"

Fig.4

Effect of DOPO content on vertical burning length of coated fabric"

Fig.5

Effect of DOPO and MCA content on limit oxygen index of coated fabric"

Tab.1

Thermogravimetric analysis data of uncoated polyamide fabric and DOPO,MCA coating fabric"

样品 T-5%/℃ Tmax/℃ 残炭量/%
聚酰胺基布 373 454 1.3
MCA (8.5%)涂层织物 361 411 2.2
DOPO(8.5%)涂层织物 337 406 4.5

Fig.6

Effect of DOPO and MCA content on stiffness of coated fabric"

Fig.7

Film formation mechanism of wet polyamide coating in presence of DOPO or MCA"

[1] 丁放, 任学宏. 磷氮阻燃剂对涤纶织物的阻燃整理[J]. 纺织学报, 2020, 41(3):100-105.
DING Fang, REN Xuehong. Flame-retardant finishing of polyester fabrics by grafting phosphorus-nitrogen compounds[J]. Journal of Textile Research, 2020, 41(3):100-105.
[2] 徐爱玲, 王春梅. 植酸的铵化及其对Lyocell织物的阻燃整理[J]. 纺织学报, 2020, 41(2):83-88.
XU Ailing, WANG Chunmei. Ammonium modification of phytic acid and flame retardant finishing of Lyocell fabric[J]. Journal of Textile Research, 2020, 41(2):83-88.
[3] 姜丽娜, 任元林. 硅烷包覆膨胀型阻燃剂共混改性粘胶纤维的研究[J]. 纺织科学与工程学报, 2020, 37(1):58-64.
JIANG Lina, REN Yuanlin. Study on modified viscose fiber blended with silane coated intumescent flame retardant[J]. Journal of Textile Science and Engineering, 2020, 37(1):58-64.
[4] 任元林, 姜丽娜, 霍同国, 等. 聚丙烯腈纤维阻燃改性研究进展[J]. 纺织学报, 2019, 40(8):181-188.
REN Yuanlin, JIANG Lina, HUO Tongguo, et al. Research progress on flame retardant modification of polyacrylonitrile fiber[J]. Journal of Textile Research, 2019, 40(8):181-188.
[5] 邓继勇, 柳芊, 董新理, 等. 新型氮-磷阻燃剂制备及其对棉织物的阻燃性能[J]. 纺织学报, 2017, 38(11):97-101.
DENG Jiyong, LIU Qian, DONG Xinli, et al. Preparation of novel N-P flame retardant and its flame retardant properties in cotton fabrics[J]. Journal of Textile Research, 2017, 38(11):97-101.
[6] 任元林, 张悦, 曾倩, 等. 织物阻燃涂层新工艺的研究进展[J]. 纺织学报, 2017, 38(9):168-173.
REN Yuanlin, ZHANG Yue, ZENG Qian, et al. Research progress of new processes of flame retardant fabrics coating[J]. Journal of Textile Research, 2017, 38(9):168-173.
[7] STANKEVICH A, MURAVSKY A, MURAUSKI A, et al. Unusual alignment during wet coating of oligo(phenylene vinylene)s thin films[J]. Molecular Crystals and Liquid Crystals, 2018, 669(1):201-206.
[8] OYANE A, NAKAMURA M, SAKAMAKI I, et al. Laser-assisted wet coating of calcium phosphate for surface-functionalization of PEEK[J]. PLOS One, 2018, 13(10):17-23.
[9] NAKAMURA S, KONDO S, MOHRI A, et al. Preparation of controlled-release particles based on spherical porous silica used as the drug carrier by the dry coating method.[J]. Journal of Pharmacy and Pharmaceutical Sciences, 2018, 19(3):123-130.
[10] 雷鹏飞, 黄亚伟, 袁森浩, 等. 油酸原位合成碳酸钙及其在聚酰胺湿法涂层中的应用[J]. 纺织学报, 2019, 40(5):70-77.
LEI Pengfei, HUANG Yawei, YUAN Senhao, et al. In-situ synjournal of calcium carbonate from oleic acid and application thereof in wet coating of polyamide[J]. Journal of Textile Research, 2019, 40(5):70-77.
[11] BRAUN U, SCHARTEL B. Flame retardancy mechanisms of aluminium phosphinate in combination with melamine cyanurate in glass-fibre-reinforced poly(1,4-butylene terephthalate)[J]. Macromolecular Materials and Engineering, 2008, 3(4):293-302.
[12] KIJOWSKA D, JANKOWSKI P, WIERZBICKA E. Halloysite modified by melamine cyanurate and its compositions based on PA6[J]. Polimery Warsaw, 2019, 64(4):259-266.
[13] JIANG H, BI M, MA D, et al. Flame suppression mechanism of aluminum dust cloud by melamine cyanurate and melamine polyphosphate[J]. Journal of Hazardous Materials, 2019, 368:368-375.
[14] ZHANG J, DUAN H, CAO J, et al. A high-efficiency DOPO-based reactive flame retardant with bi-hydroxyl for low-flammability epoxy resin[J]. Journal of Applied Polymer Science, 2020, 70(3):50165-50180.
[15] LUO Q, SUN Y, YU B, et al. Synjournal of a hyperbranched polyamide oligomer containing DOPO for simultaneously enhancing the flame retardance and glass transition temperature of epoxy resin[J]. Polymers for Advanced Technologies, 2020, 32(3):525-537.
doi: 10.1002/pat.v32.2
[16] KUNDU C K, WANG X, RAHMAN M Z, et al. Application of chitosan and DOPO derivatives in fire protection of polyamide 66 textiles: towards a combined gas phase and condensed phase activity[J]. Polymer Degradation and Stability, 2020, 176:1043-1052.
[17] HAJIBEYGI M, HABIBNEJAD N, SHABANIAN M, et al. Fabrication and study of thermal and combustion resistance of DOPO-functionalized polyamide reinforced with organo-modified Mg(OH)2 nanoparticles[J]. Polymer International, 2021, 70:317-330.
doi: 10.1002/pi.v70.3
[18] LONG L J, WANG Z, XIANG Y S, et al. Function of the aryl group in bis DOPO phosphonate on reducing fire hazards of polyamide 6 composites[J]. Journal of Applied Polymer Science, 2020, 137(39):49188-49200.
doi: 10.1002/app.v137.39
[19] 杜奕铃, 智海辉, 张龙, 等. 黑色湿法涂层商标布的制备工艺研究[J]. 现代纺织技术, 2015, 23(3):21-25.
DU Yiling, ZHI Haihui, ZHANG Long, et al. Study on preparation technology of black label fabrics in wet coating[J]. Advanced Textile Technology, 2015, 23(3):21-25.
[20] 智海辉, 张龙, 郑今欢. 聚酰胺湿法涂层浆的制备机制及其成膜性能[J]. 纺织学报, 2015, 36(9):65-69.
ZHI Haihui, ZHANG Long, ZHENG Jinhuan. Preparation mechanism and membrane properties of polyamide wet coating[J]. Journal of Textile Research, 2015, 36(9):65-69.
doi: 10.1177/004051756603600108
[21] LU X, QIAO X, TAO Y, et al. Preparation and properties of environmental friendly nonhalogen flame retardant melamine cyanurate/nylon 66 composites[J]. Journal of Applied Polymer Science, 2011, 122(3):1688-1697.
doi: 10.1002/app.34035
[1] YANG Lu, XUE Tao, MENG Jiaguang, YANG Doudou. Anion functional finish and properties of 3D printed flexible garment fabrics [J]. Journal of Textile Research, 2021, 42(08): 102-108.
[2] ZHANG Siyu, YU Li, JIA He, LIU Xin. Free form deformation modeling method and inflation mechanism of folded canopy fabrics [J]. Journal of Textile Research, 2021, 42(07): 108-114.
[3] LEI Pengfei, HUANG Yawei, YUAN Senhao, LI Hongyan, WANG Chenglong, ZHENG Jinhuan. In-situ synthesis of calcium carbonate from oleic acid and application there of in wet coating of polyamide [J]. Journal of Textile Research, 2019, 40(05): 70-77.
[4] . Influence of inorganic fillers on properties of polyamide wet-coating trademark fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2017, 38(03): 114-121.
[5] . Study on simulation of flexible fabric bend surface based on four-point interpolation method [J]. Journal of Textile Research, 2015, 36(06): 50-54.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 35 -36 .
[2] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 107 .
[3] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 109 -620 .
[4] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(01): 1 -9 .
[5] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 101 -102 .
[6] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 105 -107 .
[7] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 108 -110 .
[8] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 111 -113 .
[9] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 114 -115 .
[10] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 116 -118 .
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd