Journal of Textile Research ›› 2022, Vol. 43 ›› Issue (01): 161-166.doi: 10.13475/j.fzxb.20210102106

• Dyeing and Finishing & Chemicals • Previous Articles     Next Articles

Preparation and performance of steaming-free and washing-free printing paste with disperse dyes

FENG Bingbing1,2, LIU Yanchun1,2, ZHOU Tianchi3, BAI Gang1,2()   

  1. 1. College of Textile and Garment, Shaoxing University, Shaoxing, Zhejiang 312000, China
    2. Key Laboratory of Clean Dyeing and Finishing Technology of Zhejiang Province, Shaoxing, Zhejiang 312000, China
    3. School of Textile and Apparel, Yancheng Institute of Technology, Yancheng, Jiangsu 224051, China
  • Received:2021-01-11 Revised:2021-09-10 Online:2022-01-15 Published:2022-01-28
  • Contact: BAI Gang E-mail:gbg2000@21cn.com

RichHTML

8

PDF (PC)

48

Abstract:

In order to solve the problems of electrolyte sensitivity and color paste infiltration of synthetic thickener in printing process,thickener SX-608F, which is suitable for steaming-free and washing-free printing with disperse dyes, was prepared by screening and compounding. The viscosity, rheological properties, dye compatibility, water holding capacity was analyzed. The apparent color yield, soaping fastness and rubbing fastness of printed fabrics were tested and evaluated. The results showed that thickener SX-608F has the characteristics of pseudoplastic fluid, and the viscosity decreased with the increase of shear rate. The printing viscosity index was 0.197, the thixotropy was good and the viscosity recovery rate was 90.40%. In the frequency range of 0.1~500 rad/s, the storage modulus is larger than the loss modulus, the loss coefficient is less than 1. The printed products of SX-608F thickener have high apparent color yield compared to sodium alginate paste, the soaping fastness and rubbing fastness could reach more than 4 grade. The printing process did not require steaming and washing.

Key words: printing paste, prsteaming-free and washing-free, thickener, water holding capacity, rheology, color fastness

CLC Number: 

  • TS193.62

Tab.1

Effect of thickener type and dosage on water holding capacity and K/S value"

增稠剂 抱水性/cm K/S值
种类 质量分数/%
FL-312 1 0.35 19.24
2 0.32 21.96
3 0.10 21.33
4 0.05 21.06
RG-7202C 1 0.46 14.14
2 0.45 20.00
3 0.41 20.86
4 0.30 21.83
L-101 1 0.78 18.90
2 0.75 23.34
3 0.70 23.14
4 0.50 23.99

Tab.2

Influence of anti-seepage agent dosage on water holding capacity and K/S value"

防渗化剂质量分数/% 抱水性/cm K/S值
0 0.30 21.56
1 0.15 22.97
2 0.12 21.82
3 0.10 21.33

Tab.3

Viscosity and PVI index of thickener SX-608F with different mass fractions"

质量分
数/%		 黏度/(Pa·s) PVI指数
剪切速率为10 s-1 剪切速率为100 s-1
1 1.891 0.551 0.291
2 6.309 1.363 0.216
3 10.990 2.165 0.197
4 16.903 2.997 0.177
5 22.092 3.887 0.176

Fig.1

Apparent-viscosity shear rate curve"

Fig.2

Variation of G', G″ and tanδ with angular frequency"

Fig.3

Change of G', G″ and tanδ with shear strain"

Tab.4

Viscosity recovery rate of thickener SX-608F"

黏度/(Pa·s) 黏度回复率/%
第1阶段
剪切速率1 s-1		 第2阶段
剪切速率400 s-1		 第3阶段
剪切速率1 s-1
83.067 0.925 75.803 90.40

Fig.4

Viscosity recovery curve of SX-608F thickener"

Tab.5

Water holding capacity of color paste"

染料质量分数/% 抱水性/cm
分散红玉 分散橙 分散深蓝
1 0.01 0.01 0.01
2 0.09 0.10 0.09
3 0.15 0.12 0.14
4 0.20 0.19 0.20
5 0.30 0.25 0.25

Fig.5

Effect of disperse dyes on viscosity of thickener"

Fig.6

Effect of pH on viscosity of thickener"

Fig.7

Effect of placement time on viscosity of thickener"

Tab.6

Printing properties of thickener SX-608F"

糊料 处理方式 染料 K/S值 渗透率/% 耐摩擦色牢度/级 耐皂洗色牢度/级
正面 反面 干 湿 涤沾 棉沾 变色
海藻酸钠 还原清洗 分散红玉 16.31 9.61 58.92 5 5 4 4~5 4~5
分散橙 14.97 6.69 44.69 5 5 5 5 5
分散深蓝 20.49 8.37 40.85 5 5 4~5 4~5 4
SX-608F 未水洗 分散红玉 20.91 2.21 10.57 4~5 4 4 4~5 4
分散橙 15.61 1.84 11.79 5 5 5 5 4
分散深蓝 24.69 1.98 8.02 4~5 4 4~5 4~5 4~5
还原清洗 分散红玉 20.66 1.82 8.82 5 5 5 5 5
分散橙 15.02 1.42 9.46 5 5 5 5 5
分散深蓝 23.77 1.65 6.93 5 5 5 5 5
[1] SHIMO S S, UDDIN M Z . Energy level and chemical class of disperse dyes-plausible characteristics of level dyeing performance[J]. AATCC Journal of Research, 2021, 8(4): 15-19.
doi: 10.14504/ajr.8.4.3
[2] 张帅, 谭艳君, 霍倩. 芳纶织物分散染料印花性能探究[J]. 染整技术, 2019, 41(8): 21-24.
ZHANG Shuai, TAN Yanjun, HUO Qian. Study on printing performance of disperse dyes on aramid fabrics[J]. Textile Dyeing and Finishing Journal, 2019, 41(8): 21-24.
[3] 卜广玖, 王震, 王海生. 涤纶家纺面料的液体分散染料免洗印花[J]. 印染, 2020, 46(6): 45-49.
BU Guangjiu, WANG Zhen, WANG Haisheng. Washing-free printing of polyester home textiles with new liquid disperse dyes[J]. China Dyeing & Finishing, 2020, 46(6): 45-49.
[4] 陈智杰, 胡旭东, 黄卓. 基于细乳液法含硅颜料胶囊的制备及其对涤纶的印花性能[J]. 纺织学报, 2019, 40(8): 69-75.
CHEN Zhijie, HU Xudong, HUANG Zhuo. Preparation of silicone-containing pigment capsules by miniemulsion polymerization and printing performance thereof on polyester fabric[J]. Journal of Textile Research, 2019, 40(8): 69-75.
[5] 周律, 周宏杰. 中国印染工业废水处理与再利用的现状分析[J]. 针织工业, 2020(7): 41-46.
ZHOU lü, ZHOU Hongjie. Situation analysis wastewater treatment and reuse in China's printing and dyeing[J]. Knitting Industry, 2020(7): 41-46.
[6] 艾丽, 曹红梅, 朱亚伟. 基于液体分散染料的微量印花技术[J]. 纺织学报, 2018, 39(9): 77-83.
AI Li, CAO Hongmei, ZHU Yawei. Ultralow pollution micro-printing method based on liquid disperse dyes[J]. Journal of Textile Research, 2018, 39(9): 77-83.
[7] 胡珏, 王姜灿. 印染行业的节能分析[J]. 资源节约与环保, 2021 (4): 1-2.
HU Yu, WANG Jiangcan. Energy saving analysis of printing and dyeing industry[J]. Resource Conservation and Environmental Protection, 2021 (4): 1-2.
[8] 张乃舒. 涤纶织物免水洗印花工艺[J]. 丝网印刷, 2019 (6): 25-31.
ZHANG Naishu. Wash free printing of polyester fabric[J]. Screen Printing, 2019 (6): 25-31.
[9] 王莉莉, 陆大年. 天然印花糊料流变性能的研究[J]. 印染助剂, 2014, 31(4): 19-23.
WANG Lili, LU Danian. Study on the rheological properties of natural printing pastes[J]. Textile Auxiliaries, 2014, 31(4): 19-23.
[10] 陈英. 染整工艺实验教程[M]. 北京: 中国纺织出版社, 2008:100-101.
CHEN Ying. Dyeing and finining process of experimental course [M]. Beijing: China Textile & Apparel Press, 2008: 100-101.
[11] 李青, 苗赛男, 邢铁玲. 转移印花增稠剂的流变性与微观形貌[J]. 纺织学报, 2015, 36(9): 75-79.
LI Qing, MIAO Sainan, XING Tieling. Rheology and m orphology of thickeners in textile transfer printing[J]. Journal of Textile Research, 2015, 36(9): 75-79.
[12] 周嫦娥, 张庆, 李颖君. 用于数码印花的增稠剂的流变性能[J]. 纺织学报, 2011, 32(10): 83-87.
ZHOU Chang'e, ZHANG Qing, LI Yingjun. Rheological properties of thickeners for digital printing[J]. Journal of Textile Research, 2011, 32(10): 83-87.
doi: 10.1177/004051756203200115
[1] YU Meiqiong, YUAN Hongmei, CHEN Lihui. Rheological properties of cellulose/LiCl/ N, N-dimethylacetamide solution [J]. Journal of Textile Research, 2021, 42(05): 23-30.
[2] JI Hong, ZHANG Yang, CHEN Kang, SONG Minggen, JIANG Quan, FAN Yonggui, ZHANG Yumei, WANG Huaping. Developing black high-tenacity polyester yarns based on dynamic characteristics [J]. Journal of Textile Research, 2020, 41(04): 1-8.
[3] JIANG Hua, ZHANG Zhiheng, CAI Jinfang, CHEN Weiguo, CUI Zhihua, SUN Yanfeng. Diazotization-coupling dyeing and process control of silk fabrics by primary aryl amine dyes [J]. Journal of Textile Research, 2019, 40(11): 100-105.
[4] YE Jiahao, WANG Lili, WU Minghua, GUO Wendeng, WANG Kehao, CHEN Ni. Sizing process of silk fabric by double-sided digital ink-jet printing with same colors and designs [J]. Journal of Textile Research, 2019, 40(10): 92-97.
[5] AI Li, ZHU Yawei. Synthesis of binder and application in polyester fabric with micro-water printing of disperse blue 79 [J]. Journal of Textile Research, 2019, 40(06): 50-57.
[6] . Ultralow pollution micro-printing method based on liquid disperse dyes [J]. Journal of Textile Research, 2018, 39(09): 77-83.
[7] . Comparison of the dyeing effect of reactive dyes by salt-free continuous pad-steam dyeing and cold pad-batch dyeing [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(04): 77-81.
[8] . Thermal and dyeing properties of novel cationic-dyeable polyester fabrics under atmospheric pressure [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(12): 71-75.
[9] . Research on low damage and temperature dyeing performance of superfine wool [J]. JOURNAL OF TEXTILE RESEARCH, 2016, 37(06): 72-75.
[10] . Modification of poly (3-hydroxybutyrate-co-4-hydroxybutyrate) by epoxy-based chain extenders [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(8): 139-0.
[11] . Evaluation of rubbing color fastness to pigment printing fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(7): 90-94.
[12] . Grade evaluation of color fastness to laundering based on image analysis [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(11): 100-0.
[13] . Application of super soft pigment printing technology on cotton fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(10): 101-0.
[14] . Dyeing properties of polyester / polyamide and its cotton blended fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(10): 90-0.
[15] WANG Yan-Ping, XIA Yu-Min, GAN Hai-Xiao, ZHU Wei-Biao, QIN Wei-Min, WANG Yi-Min. Solid-phase polycondensation and melt-spinning of aromatic copolyester [J]. JOURNAL OF TEXTILE RESEARCH, 2012, 33(6): 111-115.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 35 -36 .
[2] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 107 .
[3] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 109 -620 .
[4] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 103 -104 .
[5] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 105 -107 .
[6] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 108 -110 .
[7] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 111 -113 .
[8] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 119 -120 .
[9] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(03): 7 -8 .
[10] PAN Xu-wei;GU Xin-jian;HAN Yong-sheng;CHENG Yao-dong. Research on quick response of apparel supply chain for collaboration[J]. JOURNAL OF TEXTILE RESEARCH, 2006, 27(1): 54 -57 .
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd