Journal of Textile Research ›› 2022, Vol. 43 ›› Issue (03): 103-109.doi: 10.13475/j.fzxb.20200903107

• Dyeing and Finishing & Chemicals • Previous Articles     Next Articles

Preparation and performance of allyl polyalkoxy epoxy ether

YANG Zhensheng1,2(), WANG Bingshuai2   

  1. 1. School of Petrochemical Engineering, Shenyang University of Technology, Liaoyang, Liaoning 111003, China
    2. Liaoning Kelong Fine Chemical Co., Ltd., Liaoyang, Liaoning 111013, China
  • Received:2020-09-15 Revised:2021-12-30 Online:2022-03-15 Published:2022-03-29

RichHTML

18

PDF (PC)

92

Abstract:

Targeting at the poor reactive activity in preparing terpolymer block silicone oil caused by high contents of catalyst,potassium and sodium ions in allyl polyalkoxy epoxy ether, the preparation of allyl polyalkoxy epoxy ether without transfer catalyst was studied. The structure of the product was characterized, and the effect of preparation conditions on pH value and epoxy index of the product were analyzed. Terpolymer block silicone oil was prepared from it and was used to soften the fabric. And hydrophilicity, hand feeling, physical and mechanical properties of finished fabric were studied. The results show that when the molar ratio of raw material allyl polyoxyethylene oxide/ECH/sodium hydroxide is 1∶2.5∶1.5 and the amount of glacial acetic acid added is 1.1 times that of excessive base, the epoxy index is 1.77 mol/kg, the pH value is less than 7, and the content of potassium and sodium ions is reduced to less than 5 μg/g after refining. And the fabric has good hydrophilicity after finishing with silicone oil. The capillary effect reaches 7.3 cm and the fabric handle reaches grade 4.7 when the finishing liquid mass concentration is 30 g/L, and the overall performance of the fabric is improved.

Key words: softening agent, terpolymer block silicone oil, allyl polyalkoxy epoxy ether, non-phase-transfer, capillary effect, hydrophilicity

CLC Number: 

  • TS101

Fig.1

Effect of phase transfer catalyst on epoxy index"

Fig.2

Phase transfer process of reactants"

Tab.1

Effect of reaction material molar ratio on epoxy index of product"

序号 反应原料的量/mol 环氧指数/
(mol·kg-1)
烯丙基聚氧乙烯醚 环氧氯丙烷 氢氧化钠
1 0.10 0.10 0.10 0.73
2 0.10 0.15 0.10 1.13
3 0.10 0.20 0.10 1.35
4 0.10 0.25 0.10 1.51
5 0.10 0.25 0.12 1.63
6 0.10 0.25 0.15 1.77
7 0.10 0.30 0.15 1.78
8 0.10 0.30 0.20 1.78

Tab.2

Effect of acetic acid content on pH value and unsaturation degree of product"

序号 冰醋酸的量/mol 产物pH值 产物不饱和度/(mol·kg-1)
1 0.000 8.6 1.75
2 0.040 7.5 1.75
3 0.045 7.3 1.74
4 0.050 7.1 1.74
5 0.055 6.7 1.74
6 0.060 6.5 1.73
7 0.064 6.4 1.73

Tab.3

Effect of phosphoric acid content on pH value and unsaturation degree of product"

序号 磷酸的量/mol 产物pH值 产物不饱和度/(mol·kg-1)
1 0.000 8.6 1.75
2 0.013 7.8 1.75
3 0.015 7.7 1.73
4 0.017 7.4 1.65
5 0.018 7.3 1.62
6 0.020 7.1 1.60
7 0.022 7.1 1.59

Fig.3

Side reaction process of phosphoric acid and allyl polyalkoxy epoxy ether"

Tab.4

Effect of distilled water and adsorbent on content of K+and Na+"

序号 蒸馏水质
量分数/%		 吸附剂质
量分数/%		 K+含量/
(μg·g-1)		 Na+含量/
(μg·g-1)
1 0 0 103 130.0
2 3 0.10 23 31.0
3 4 0.15 9 7.0
4 5 0.15 4 3.0
5 5 0.20 1 0.6

Fig.4

IR spectrum of allyl polyalkoxy epoxy ether"

Fig.5

H-NMR spectra of allyl polyalkoxy epoxy ether"

Fig.6

Effect of concentration of finishing liquid on fabric hydrophilicity"

Tab.5

Comparison of finishing and grading effects of terpolymer block silicone oil emulsions prepared with different hydrogen-containing silicone oils"

整理液质量浓度/
(g·L-1)		 手感评级/级
整理液a 整理液b
0 2.8 2.8
10 3.9 4.3
20 4.3 4.7
30 4.7 4.9
40 4.7 4.9

Tab.6

Basic physical and mechanical properties of fabrics by KES tests"

样品 LT WT RT G 2HG 2HG5 B 2HB LC WC RC T0 W MIU MMD SMD
1 0.751 3 11.254 42.856 1.854 3.140 6.954 0.073 6 0.072 1 0.706 3 0.186 4 48.64 0.453 6 6.92 0.135 4 0.013 2 3.864 2
2 0.695 3 10.981 54.169 1.346 0.914 2.169 0.026 4 0.025 1 0.272 1 0.164 9 46.84 0.450 1 6.95 0.086 2 0.013 2 1.468 1
[1] 刘彦杰, 吴明华, 侯彦敏, 等. 超支化氨基改性聚硅氧烷的合成及其应用[J]. 纺织学报, 2014,35(12):73-79.
LIU Yanjie, WU Minghua, HOU Yanmin, et al. Synjournal and application of hyperbranched amino modified polysiloxane[J]. Journal of Textile Research, 2014,35(12):73-79.
doi: 10.1177/004051756503500108
[2] 王小娟. 有机硅柔软剂的发展及应用[J]. 印染, 2020,42(6):10-13.
WANG Xiaojuan. Development and application of silicone softener[J]. China Dyeing & Finishing, 2020,42(6):10-13.
[3] 鲁涛, 游奎一, 易兵, 等. 新型三元共聚嵌段硅油的合成及应用[J]. 印染, 2016,42(16):39-42.
LU Tao, YOU Kuiyi, YI Bing, et al. Synjournal and application of a new type terpolymer block silicone oil[J]. China Dyeing & Finishing, 2016,42(16) :39-42.
[4] YUAN W, CHENG Z, PENG C, et al. Synjournal of multiblock linear polyether functional amino silicone softener and its modification of surface properties on cotton fabrics[J]. Polymer Bulletin, 2019,76(1):447-467.
doi: 10.1007/s00289-018-2375-1
[5] JASON P M, WAKE F, JACOB W, et al. Method for enzymatic treatment of wool: US, 6051033[P]. 2000-04-18.
[6] MOHAMMAD M A, AMIN J, REZA T, et al. Processing and performance properties of amino silicone-based softener on various textile substrates[J]. Polymer Bulletin, 2020,77(5):2557-2572.
doi: 10.1007/s00289-019-02877-x
[7] 王娟, 宋秘钊, 刘玉龙. 有机硅柔软剂的研究进展[J]. 应用化工, 2020,49(2):458-461.
WANG Juan, SONG Mizhao, LIU Yulong. Research progress of silicone softeners[J]. Applied Chemical Industry, 2020,49(2):458-461.
[8] 王小娟. 聚醚改性有机硅柔软剂的合成[J]. 轻纺工业与技术, 2020,49(9):6-8.
WANG Xiaojuan. Synjournal of polyether modified organosilicone softener[J]. Light and Textile Industry and Technology, 2020,49(9):6-8.
[9] 王彦珍, 宋秘钊, 王娟, 等. 氨基聚醚改性硅油柔软剂在亚麻织物上的应用[J]. 棉纺织技术, 2021,49(10):38-41.
WANG Yanzhen, SONG Mizhao, WANG Juan, et al. Application of amino polyether modified silicone oil softener on flax fabric[J]. Cotton Textile Technology, 2021,49(10):38-41.
[10] 于岩, 章若红, 钟毅, 等. 用气相色谱-质谱法测定纺织柔软剂中的环硅氧烷[J]. 纺织学报, 2020,41(8):69-73.
YU Yan, ZHANG Ruohong, ZHONG Yi, et al. Determination of cyclicsilicates in textile softeners by gas chromatography-mass spectrometry[J]. Journal of Textile Research, 2020,41(8):69-73.
[11] 陈焜, 周向东. 有机硅柔软剂的结构、性能、表征及其吸附模型[J]. 印染助剂, 2019,36(9):7-12.
CHEN Kun, ZHOU Xiangdong. Structure, performance, characterization and adsorption model of silicone softener[J]. Textile Auxiliaries, 2019,36(9):7-12.
[12] CZECH A M, PAVLENYI J, SABIA A J. Modified silicone softeners for fluorocarbon soil release treatments[J]. Textile Chemist and Colorist, 1997,29(9):26-29.
[13] 马现奇, 尹红, 袁慎峰, 等. 氨基硅油柔软剂作用模型的研究进展[J]. 印染助剂, 2011,28(8):1-7.
MA Xianqi, YIN Hong, YUAN Shenfeng, et al. Study on progress of working model of amino silicone softener[J]. Textile Auxiliaries, 2011,28(8):1-7.
[14] 鲁涛, 游奎一, 易兵, 等. 新型三元共聚嵌段硅油的合成及应用研究[J]. 纺织科技进展, 2016(8):15-18.
LU Tao, YOU Kuiyi, YI Bing, et al. Synjournal and application of a new type terpolymer block silicone[J]. Progress in Textile Science and Technology, 2016(8):15-18.
[15] 周勇. 三元嵌段有机硅柔软剂的制备及其在纺织品上的应用[D]. 广州:华南理工大学, 2017:4-6.
ZHOU Yong. Preparation of ternary block silicone softener and its application in textiles[D]. Guangzhou: South China University of Technology, 2017:4-6.
[1] GAO Qiang, WANG Xiao, GUO Yajie, CHEN Ru, WEI Ju. Preparation and performance of cotton based Ti3C2Tx oil-water separation membrane [J]. Journal of Textile Research, 2022, 43(01): 172-177.
[2] ZHANG Huan, YAN Jun, WANG Xiaowu, JIAO Andong, LI Hong, ZHENG Laijiu, HE Tingting. Application of low temperature plasma in surface modification of polyester fiber [J]. Journal of Textile Research, 2019, 40(07): 103-107.
[3] LI Bing, GE Guoping, GUO Wei, DONG Yongchun, CHEN Xingcan. Comparison between structure and performance of fresh cocoon raw silk and dry cocoon raw silk and identification method thereof [J]. Journal of Textile Research, 2019, 40(03): 32-38.
[4] JIA Huiying, JIANG Zhiqing, MA Jianwei, JIANG Liang, CHEN Shaojuan. Preparation and properties of modified polytetrafluoroethylene fiber by oxidation self-polymerization of dopamine [J]. Journal of Textile Research, 2019, 40(01): 14-18.
[5] . Effect of modified by β-cyclodextrin derivatives of aldehydes crosslinked chitosan on hydrophilicity of polyester fabric [J]. JOURNAL OF TEXTILE RESEARCH, 2018, 39(07): 82-88.
[6] . Development of unidirectional water-transfer fabrics [J]. Journal of Textile Research, 2016, 37(05): 167-172.
[7] . Preparation and properties of jute/soybean dregs/starch composites [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(8): 44-0.
[8] . Preparation of highly hydrophilic polyester fabric with ionic reagent [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(6): 45-0.
[9] . Preparation of amino silicone softener modified by polyurethane prepolymer [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(3): 87-0.
[10] . Property of hydrophilic PMMA/β-CD nanofibers and its adsorption properties of Cu2+ [J]. JOURNAL OF TEXTILE RESEARCH, 2014, 35(11): 19-0.
[11] . Capillary effect and moisture absorption and liberation property of yarns blended with some environment friendly fibers [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(9): 34-0.
[12] . Preparation and properties of new flame retardant hydrophilic polyester [J]. JOURNAL OF TEXTILE RESEARCH, 2013, 34(2): 18-22.
[13] LI Xu-Ming, CAO Chan-Zhen, CHEN Gui-Yun, CHEN Li-Xiao. Influence of Plasma Treatment on Hydrophilicity of Raw Cotton Fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2011, 32(12): 24-27.
[14] CHEN Ying;CHEN Sen;SONG Fujia. Ar plasma initiated grafting reaction for hydrophilicity of PET fabrics [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(7): 74-78.
[15] TANG Lihua;REN Wanting; LI Xin;WANG Rongmin. Hydrophilic modification of PP nonwoven fabric by cold plasma [J]. JOURNAL OF TEXTILE RESEARCH, 2010, 31(4): 30-34.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd