Preparation and properties of Si/TiO2 composite carbon nanofibers

XING Yusheng1,2, HU Yi1,2(), CHENG Zhongling1,2   

  1. 1. Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou, Zhejiang 310018, China
    2. Engineering Research Center for Eco-Dyeing & Finishing of Textiles, Zhejiang Sci-Tech University, Hangzhou, Zhejiang 310018, China
  • Received:2020-05-08 Revised:2020-12-15 Online:2021-03-15 Published:2021-03-17
  • Contact: HU Yi E-mail:huyi-v@zstu.edu.cn

RichHTML

11

PDF (PC)

110

Abstract:

In order to improve the morphology and structure of silicon/carbon nanofibers and enhance their energy storage performance, Si/TiO2/PAN nanofiber membranes was prepared though electrospinning of the ball milling Si/TiO2 powder and polyacrylonitrile(PAN), and then in an argon or hydrogen atmosphere carbonization treatment was carried out to obtain Si/TiO2 composite carbon nanofibers. The most suitable ratio of Si to TiO2 and carbonization temperature were optimized, the influence of fiber morphology, molecular structure, and element distribution on energy storage performance were analyzed. As a result, Si/TiO2 composite carbon nanofibers with good conductivity were prepared under the conditions of 1∶2 mass ratio between Si and TiO2 and 900 ℃ carbonization temperature. The fiber structure and the formed TiO2 disordered framework were able to ease effectively the volume expansion and agglomeration of silicon, significantly improving the capacity and cycle stability of lithium-ion batteries. At 0.2 mA/g current density and after 120 cycles, the discharge specific capacities of the composite carbon nanofibers prepared by argon and hydrogen carbonization were 942 and 1 212 mA·h/g, respectively. The work showed that the composite carbon nanofibers prepared through hydrogen carbonization have better rate performance.

Key words: composite carbon nanofibers, functional fiber, energy storage fiber, electrospinning, carbonization, ball milling mixing, electrochemical performance

CLC Number: 

  • TS195

Fig.1

SEM and TEM images of Si and TiO2 nanoparticles. (a) SEM image of Si nanoparticle; (b) SEM image of TiO2 nanoparticles; (c) TEM image of Si nanoparticle; (d) TEM image of TiO2 nanoparticles"

Fig.2

SEM images of Si/TiO2 composite carbon nanofibers with different mass ratios of Si and TiO2"

Fig.3

Energy storage performance of Si/TiO2 composite carbon nanofibers with different mass ratios of Si and TiO2"

Fig.4

SEM images of Si/TiO2composite carbon nanofibers with different carbonization temperatures"

Fig.5

XRD patterns and TEM images of Si/TiO2 composite carbon nanofibers prepared by carbonization under Ar atmosphere. (a) XRD pattern; (b) TEM images; (c) Selected area electron diffraction images"

Fig.6

Raman spectra of Si/TiO2 composite carbon nanofibers prepared by carbonization under Ar atmosphere. (a) Raman spectrum; (b) Partly enlarged view of Raman spectrum"

Fig.7

XPS spectra of Si/TiO2 composite carbon nanofibers prepared by carbonization under Ar atmosphere. (a) XPS spectrum; (b) O 1s spectrogram; (c) Ti 2p spectrogram"

Fig.8

SEM(a)and TEM(b)images of Si/TiO2 composite carbon nanofibers prepared by carbonization under H2 atmosphere"

Fig.9

Raman spectra of composite carbon nanofibers prepared by carbonization under H2 atmosphere. (a) Raman spectrum; (b) Partly enlarged view of Raman spectrum"

Fig.10

XPS spectrum of composite carbon nanofibers prepared by carbonization under H2 atmosphere. (a) XPS spectrum; (b) O 1s spectrogram;(c) Ti 2p spectrogram"

Fig.11

Thermogravimetric analysis curve of Si/TiO2 composite carbon nanofibers"

Fig.12

Electrochemical performance of Si/TiO2 composite carbon nanofibers prepared by carbonization in different atmospheres. (a)Energy storage performance curve (Ar); (b) Energy storage performance curve (H2); (c) Electrochemical impedance spectroscopy"

[1] DAI K, BERGOT A, LIANG C, et al. Environmental issues associated with wind energy:a review[J]. Renewable Energy, 2015,75:911-921.
[2] 陈成钧. 太阳能和风能的短期分散储存[J]. 物理, 2009,38(2):84-91.
CHEN Chengjun. Short-term decentralized storage of solar and wind energy[J]. Physics, 2009,38(2):84-91.
[3] 邓丽丹. 基于Spring MVC的电力新能源基础数据管理与分析系统[D]. 南昌:江西农业大学, 2014: 27-55.
DENG Lidan. Spring MVC-based power new energy basic data management and analysis system[D]. Nanchang:Jiangxi Agricultural University, 2014: 27-55.
[4] 谢娇, 王家俊, 俞秋燕, 等. 碳纳米管/聚合物温差发电复合纺织材料的制备及其性能[J]. 纺织学报, 2018,39(11):55-60.
XIE Jiao, WANG Jiajun, YU Qiuyan, et al. Preparation and properties of carbon nanotube/polymer thermoelectric composite textile materials[J]. Journal of Textile Research, 2018,39(11):55-60.
[5] 赵金洋, 孙窈, 张鑫, 等. 锡/碳纳米纤维锂电负极材料形貌结构再造及其机制[J]. 纺织学报, 2019,40(8):7-13.
ZHAO Jinyang, SUN Yao, ZHANG Xin, et al. Reconstruction of morphology and structure of tin/carbon nanofiber lithium anode materials and its mechanism[J]. Journal of Textile Research, 2019,40(8):7-13.
[6] 田银彩, 张浩鹏, 李博琛, 等. 静电纺聚丙烯腈/石墨烯碳纳米纤维的结构与性能[J]. 纺织学报, 2018,39(10):24-31.
TIAN Yincai, ZHANG Haopeng, LI Bochen, et al. Structure and properties of electrospun polyacrylonitrile/graphene carbon nanofibers[J]. Journal of Textile Research, 2018,39(10):24-31.
doi: 10.1177/004051756903900104
[7] 魏来. 锂离子电池硅基负极材料的制备与改性研究[D]. 长沙:中南大学, 2014: 5-35.
WEI Lai. Preparation and modification of silicon-based anode materials for lithium-ion batteries[D]. Changsha:Central South University, 2014: 5-35.
[8] DU F, NI Y, WANG Y, et al. Green fabrication of silkworm cocoon-like silicon-based composite for high-performance Li-ion batteries[J]. ACS Nano, 2017,11(9):8628-8635.
doi: 10.1021/acsnano.7b03830 pmid: 28800223
[9] XIAO B, SOTO F, GU M, et al. Lithium-pretreated hard carbon as high-performance sodium-ion battery anodes[J]. Advanced Energy Materials, 2018,8(24):1801441.
doi: 10.1002/aenm.v8.24
[10] NIE P, LE Z, CHEN G, et al. Graphene caging silicon particles for high-performance lithium-ion batteries[J]. Small, 2018,14(25):1800635.
doi: 10.1002/smll.v14.25
[11] XU Q, LI J, SUN J, et al. Watermelon-inspired Si/C microspheres with hierarchical buffer structures for densely compacted lithium-ion battery anodes[J]. Advanced Energy Materials, 2017,7(3):1601481.
doi: 10.1002/aenm.201601481
[12] LI B, LI S, JIN Y, et al. Porous Si@C ball-in-ball hollow spheres for lithium-ion capacitors with improved energy and power densities[J]. Journal of Materials Chemistry A, 2018,6(42):21098-21103.
doi: 10.1039/C8TA07576J
[13] LIANG G, QIN X, ZOU J, et al. Electrosprayed silicon-embedded porous carbon microspheres as lithium-ion battery anodes with exceptional rate capacities[J]. Carbon, 2018(127):424-431.
[14] CHEN H, HOU X, CHEN F, et al. Milled flake graphite/plasma nano-silicon@carbon composite with void sandwich structure for high performance as lithium ion battery anode at high temperature[J]. Carbon, 2018(130):433-440.
[15] XU R, WANG G, ZHOU T, et al. Rational design of Si@carbon with robust hierarchically porous custard-apple-like structure to boost lithium storage[J]. Nano Energy, 2017,39:253-261.
[16] YANG J, WANG Y, LI W, et al. Amorphous TiO2 shells: a vital elastic buffering layer on silicon nanoparticles for high-performance and safe lithium storage[J]. Advanced Materials, 2017(4):1700523.
[17] HUANG S, ZHANG L, LIU L, et al. Rationally engineered amorphous TiOx/Si/TiOx nanomembrane as an anode material for high energy lithium ion battery[J]. Energy Storage Materials, 2018,12:23-29.
[1] CHENG Yue, AN Qi, LI Dawei, FU Yijun, ZHANG Wei, ZHANG Yu. Preparation of SiO2 in-situ doped polyvinylidene fluoride nanofiber membrane and its properties [J]. Journal of Textile Research, 2021, 42(03): 71-76.
[2] ZHANG Yike, JIA Fan, GUI Cheng, JIN Rui, LI Rong. Preparation and piezoelectric properties of carbon nanotubes/polyvinylidene fluoride nanofiber membrane [J]. Journal of Textile Research, 2021, 42(03): 44-49.
[3] GUO Xuesong, GU Jiayi, HU Jianchen, WEI Zhenzhen, ZHAO Yan. Preparation and properties of polyacrylonitrile/carboxyl styrene butadiene latex composite nanofibrous membranes [J]. Journal of Textile Research, 2021, 42(02): 34-40.
[4] CHEN Yunbo, ZHU Xiangyu, LI Xiang, YU Hong, LI Weidong, XU Hong, SUI Xiaofeng. Recent advance in preparation of thermo-regulating textiles based on phase change materials [J]. Journal of Textile Research, 2021, 42(01): 167-174.
[5] WANG He, WANG Hongjie, RUAN Fangtao, FENG Quan. Preparation and properties of carbon nanofiber electrode made from electrospun polyacrylonitrile/linear phenolic resin [J]. Journal of Textile Research, 2021, 42(01): 22-29.
[6] YANG Gang, LI Haidi, QIAO Yansha, LI Yan, WANG Lu, HE Hongbing. Preparation and characterization of polylactic acid-caprolactone/fibrinogen nanofiber based hernia mesh [J]. Journal of Textile Research, 2021, 42(01): 40-45.
[7] YANG Yuchen, QIN Xiaohong, YU Jianyong. Research progress of transforming electrospun nanofibers into functional yarns [J]. Journal of Textile Research, 2021, 42(01): 1-9.
[8] WANG Ximing, CHENG Feng, GAO Jing, WANG Lu. Effect of cross-linking modification on properties of chitosan/polyoxyethylene nanofiber membranes towards wound care [J]. Journal of Textile Research, 2020, 41(12): 31-36.
[9] ZHANG Yike, JIA Fan, GUI Cheng, JIN Rui, LI Rong. Preparation and performance of flexible sensor made from polyvinylidene fluoride/FeCl3 composite fibrous membranes [J]. Journal of Textile Research, 2020, 41(12): 13-20.
[10] WANG Liyuan, KANG Weimin, ZHUANG Xupin, JU Jingge, CHENG Bowen. Preparation and properties of composite proton exchange membranes based on sulfonated polyethersulfone nanofibers [J]. Journal of Textile Research, 2020, 41(11): 19-26.
[11] LI Haoyi, XU Hao, CHEN Mingjun, YANG Tao, CHEN Xiaoqing, YAN Hua, YANG Weimin. Research progress of noise reduction by nanofibers [J]. Journal of Textile Research, 2020, 41(11): 168-173.
[12] WANG Zixi, HU Yi. Preparation and energy storage of porous carbon nanofibers based on ZnCo2O4 [J]. Journal of Textile Research, 2020, 41(11): 10-18.
[13] PAN Lu, CHENG Tingting, XU Lan. Preparation of polycaprolactone/polyethylene glycol nanofiber membranes with large pore sizes and its application for tissue engineering scaffold [J]. Journal of Textile Research, 2020, 41(09): 167-173.
[14] YANG Kai, ZHANG Xiaomei, JIAO Mingli, JIA Wanshun, DIAO Quan, LI Yong, ZHANG Caiyun, CAO Jian. Preparation and adsorption performance of high-ortho phenolic resin based activated carbon nanofibers [J]. Journal of Textile Research, 2020, 41(08): 1-8.
[15] WU Hong, LIU Chengkun, MAO Xue, YANG Zhi, CHEN Meiyu. Research progress in preparation and application of flexible zirconia nanofibers by electrospinning [J]. Journal of Textile Research, 2020, 41(07): 167-173.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd