Journal of Textile Research ›› 2021, Vol. 42 ›› Issue (11): 17-23.doi: 10.13475/j.fzxb.20201102007

• Fiber Materials • Previous Articles     Next Articles

Preparation and microstructure control of aerogel fibers based on aramid nanofibers

CHEN Xian1,2, LI Mengmeng1,2, ZHAO Xin1,2, DONG Jie1,2, TENG Cuiqing1,2()   

  1. 1. College of Materials Science and Engineering, Donghua University, Shanghai 201620, China
    2. State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University, Shanghai 201620, China
  • Received:2020-11-20 Revised:2021-07-22 Online:2021-11-15 Published:2021-11-29
  • Contact: TENG Cuiqing E-mail:cqteng@dhu.edu.cn

RichHTML

37

PDF (PC)

230

Abstract:

In order to further improve the mechanical strength of aerogel fibers, the dispersion solution of aramid nanofibers was prepared with para aramid fiber as raw materials, and aerogel fibers based on aramid nanofibers were fabricated via wet spinning, solvent displacement and following freeze-drying processes. The microstructures of aerogel fibers based on aramid nanofibers were also adjusted by changing the percentage of tertiary butyl alcohol and water in the solvent replacement bath. The results showed that the change of solvent replacement bath could give the aerogel fibers good formability. When the volumetric ratio of tert-butanol to water in the solvent replacement bath was 1∶1, the aerogel fiber had a fluffy network structure in the interior,its specific surface area reached 165.4 m2/g and the fracture strength was 4.8 MPa. With the increase of water content, the specific surface area of aerogel fibers decreased with enhanced the mechanical strength. When only water was used as the solvent replacement solution, the aramid nanofibers were neatly orientated in the fiber length direction, and the fracture strength of aerogel fibers reached 328.7 MPa.

Key words: aramid nanofiber, aerogel fiber, wet spinning, solvent replacement, freeze drying, high-performance fiber

CLC Number: 

  • TS430

Fig.1

Schematic diagram of preparation process of nano-aramid aerogel fibers"

Fig.2

Preparation process (a) and its mechanisms (b) of nano-aramid"

Fig.3

TEM image of nano-aramid"

Fig.4

FT-IR (a) and XRD (b) curves of aramid and nano-aramid"

Fig.5

SEM images of cross section and surface section of 2#-5# nano-aramid aerogel fibers"

Fig.6

SEM images of surface (a)and cross section (b) of 1# nano-aramid aerogel fibers"

Fig.7

Shrinkage-specific surface area (a) and porosity (b) for various nano-aramid aerogel fibers under different conditions"

Tab.1

Density of nano-aramid aerogel fibers"

样品编号 密度/(mg·cm-3) 样品编号 密度/(mg·cm-3)
1# 812 4# 91
2# 35 5# 136
3# 50

Fig.8

Stress-strain curves of 2#-5# and 1# nano-aramid aerogel fibers under different preparation conditions"

[1] KINOSHITAM, SUGAMURA T, SHIMOYAMA Y. Effect of solvent species inside wet gel on fabrication of titania nanoparticle by supercritical carbon dioxide drying[J]. Journal of Supercritical Fluids, 2016, 110:90-96.
doi: 10.1016/j.supflu.2015.12.015
[2] KUNANUSONT N, SHIMOYAMA Y. Porous carbon electrode for Li-air battery fabricated from solvent expansion during supercritical drying[J]. Journal of Supercritical Fluids, 2017, 133:77-85.
doi: 10.1016/j.supflu.2017.09.030
[3] ZHAO H B, CHEN M, CHEN H B. Thermally insulating and flame-retardant polyaniline/pectin aerogels[J]. ACS Sustainable Chemistry & Engineering, 2017, 5(8):7012-7019.
[4] LU A, WAND J Y, DONALD P, et al. An all-ceramic, anisotropic, and flexible aerogel insulation material[J]. Nano Letters, 2020, 20(5):3828-3835.
doi: 10.1021/acs.nanolett.0c00917
[5] CHEN X, LIU H, ZHENG Y, et al. Highly compressible and robust polyimide/carbon nanotube composite aerogel for high-performance wearable pressure sensor[J]. ACS Applied Materials & Interfaces, 2019, 11(45):42594-42606.
[6] WU T, DONG J, GAN F, et al. Low dielectric constant and moisture-resistant polyimide aerogels containing trifluoromethyl pendent groups[J]. Applied Surface Science, 2018, 440:595-605.
doi: 10.1016/j.apsusc.2018.01.132
[7] MEADOR M B, AGNELLO M, MCCORKLE L, et al. Moisture-resistant polyimide aerogels containing propylene oxide links in the backbone[J]. ACS Applied Materials & Interfaces, 2016, 8(42):29073-29079.
[8] ZHANG J, CHENG Y, TEBYETEKERWA M, et al. "Stiff-soft" binary synergistic aerogels with superflexibility and high thermal insulation performance[J]. Advanced Functional Materials, 2019, 29(15):1806407.
doi: 10.1002/adfm.v29.15
[9] LEE T W, LEE S E, JEONG Y G. Highly effective electromagnetic interference shielding materials based on silver nanowire/cellulose papers[J]. ACS Applied Materials & Interfaces, 2016, 8(20):13123-13132.
[10] ZENG Z, WU T, HAN D, et al. Ultralight, flexible, and biomimetic nanocellulose/silver nanowire aerogels for electromagnetic interference shielding[J]. ACS Nano, 2020, 14(3):2927-2938.
doi: 10.1021/acsnano.9b07452
[11] HAO P, ZHAO Z, LENG Y, et al. Graphene-based nitrogen self-doped hierarchical porous carbon aerogels derived from chitosan for high performance supercapacitors[J]. Nano Energy, 2015, 15:9-23.
doi: 10.1016/j.nanoen.2015.02.035
[12] DU Y, ZHANG X, WANG J, et al. Reaction-spun transparent silica aerogel fibers[J]. ACS Nano, 2020, 14(9):11919-11928.
doi: 10.1021/acsnano.0c05016
[13] YANG M, CAO K, SUI L, et al. Dispersions of aramid nanofibers: a new nanoscale building block[J]. ACS Nano, 2011, 5(9):6945-6954.
doi: 10.1021/nn2014003
[14] LI Y, KANG Z, YAN X, et al. Three-dimensional reticulate CNT-aerogel for high mechanical flexibility fiber supercapacitor[J]. Nanoscale, 2018, 10(19):9360-9368.
doi: 10.1039/C8NR01991F
[15] WANG H, DONG Q, YAO J, et al. Colorless silk/copper sulfide hybrid fiber and fabric with spontaneous heating property under sunlight[J]. Biomacromolecules, 2020, 21(4):1596-1603.
doi: 10.1021/acs.biomac.0c00170
[16] WANG Z, YANG H, LI Y, et al. Robust silk fibroin/graphene oxide aerogel fiber for radiative heating textiles[J]. ACS Applied Materials & Interfaces, 2020, 12(13):15726-15736.
[17] DEWILDE S, WINTERS J, DEHAEN W, et al. Polymerization of PPTA in ionic liquid/cosolvent mixtures[J]. Macromolecules, 2017, 50(8):3089-3100.
doi: 10.1021/acs.macromol.7b00579
[18] BENZAIT Z, TRABZON L. A review of recent research on materials used in polymer-matrix composites for body armor application[J]. Journal of Composite Materials, 2018, 52(23):3241-3263.
doi: 10.1177/0021998318764002
[19] 刘克杰, 杨琴. 有机特种纤维介绍[J]. 合成纤维, 2013, 42(1):25-29.
LIU Kejie, YANG Qin. Introduction to organic special fibers[J]. Synthetic Fibre in China, 2013, 42(1):25-29.
[20] ZHOU J, HSIEH Y L. Nanocellulose aerogel-based porous coaxial fibers for thermal insulation[J]. Nano Energy, 2019, 68:104305.
doi: 10.1016/j.nanoen.2019.104305
[21] 杜松, 左建国, 邓英杰. 叔丁醇-水共溶剂冷冻干燥工艺及其在药剂学中的应用[J]. 中国药剂学杂志(网络版), 2006(3):116-121.
DU Song, ZUO Jianguo, DENG Yingjie. Tert-butanol-water co-solvent freeze-drying process and its application in pharmacy[J]. Chinese Journal of Pharmacy, 2006(3):116-121.
[22] KARADAGLI I, SCHULZ B, SCHESTAKOW M, et al. Production of porous cellulose aerogel fibers by an extrusion process[J]. Journal of Supercritical Fluids, 2015, 106:105-114.
doi: 10.1016/j.supflu.2015.06.011
[23] LIU Z, LYU J, FAND D, et al. Nanofibrous Kevlar aerogel threads for thermal insulation in harsh environments[J]. ACS Nano, 2019, 13(5):5703-5711.
doi: 10.1021/acsnano.9b01094
[24] WANG F, WU Y, HUANG Y. High strength, thermostable and fast-drying hybrid transparent membranes with POSS nanoparticles aligned on aramid nanofibers[J]. Composites Part A: Applied Science and Manufacturing, 2018, 110:154-161.
doi: 10.1016/j.compositesa.2018.04.031
[1] CHEN Zihan, YAO Yongbo, SHENG Junlu, YAN Zhiyong, ZHANG Yumei, WANG Huaping. Preparation and properties of cellulose/calcium alginate blend fiber [J]. Journal of Textile Research, 2021, 42(12): 15-20.
[2] LIU Qiangfei, WU Shaohua, YANG Jizhen, ZHOU Rong, DONG Xianglin, SONG Chuanbo, SHEN Zhaoxu. Preparation and properties of polytetrafluoroethylene/phenylene sulfide needled felt modified by aramid nanofiber [J]. Journal of Textile Research, 2021, 42(10): 47-52.
[3] WANG Huiyun, WANG Ping, LI Yuanyuan, ZHANG Yan. Preparation of polyacrylonitrile hollow porous shaped fibers and its performance [J]. Journal of Textile Research, 2021, 42(03): 50-55.
[4] LIU Shuqiang, WU Jie, WU Gaihong, YIN Xiaolong, LI Fu, ZHANG Man. Surface modification of basalt fiber using nano-SiO2 [J]. Journal of Textile Research, 2020, 41(12): 37-41.
[5] MA Yue, GUO Jing, YIN Juhui, ZHAO Miao, GONG Yumei. Preparation and characterization of cellulose/dialdehyde cellulose/Antarctic krill protein antibacterial fibers [J]. Journal of Textile Research, 2020, 41(11): 34-40.
[6] YANG Yaru, SHEN Xiaojun, TANG Bolin, NIU Mei. Halogen-free flame retardant finishing of ultra-high molecular weight polyethylene fiber [J]. Journal of Textile Research, 2020, 41(11): 109-115.
[7] PANG Yali, MENG Jiayi, LI Xin, ZHANG Qun, CHEN Yankun. Preparation of graphene fibers by wet spinning and fiber characterization [J]. Journal of Textile Research, 2020, 41(09): 1-7.
[8] ZHAN Xiaoqing, LI Fengyan, ZHAO Jian, LI Haiqiong. Thermal mechanical stability of ultrahigh molecular weight polyethylene fiber [J]. Journal of Textile Research, 2020, 41(08): 9-14.
[9] WAN Yucai, LIU Ying, WANG Xu, YI Zhibing, LIU Ke, WANG Dong. Structure and property of poly(vinyl alcohol-co-ethylene) nanofiber/polypropylene microfiber scaffold: a composite air filter with high filtration performance [J]. Journal of Textile Research, 2020, 41(04): 15-20.
[10] YUE Chengfei, DING Changkun, LI Lu, CHENG Bowen. Carbodiimide/hydroxysuccinimide crosslinking modification and properties of collagen fibers [J]. Journal of Textile Research, 2020, 41(03): 1-7.
[11] SONG Le, SHEN Lanping, HUANG Xianwen, HENG Fangfang, MA Hongbo, OUYANG Qin, CHEN Peng, WANG Xuan. Preparation and properties of lignin/polyacrylonitrile composite fibers [J]. Journal of Textile Research, 2020, 41(02): 7-12.
[12] OUYANG Pengfei, ZHANG Yufang, JIA Chunzi, ZHANG Jiayu. Properties of regenerated fibers from bamboo pulp/ionic liquid combined system [J]. Journal of Textile Research, 2020, 41(01): 21-25.
[13] LI Zhenqun, XU Duo, WEI Chunyan, QIAN Yongfang, LÜ Lihua. Preparation of cotton stalk bast cellulose/graphene oxide fiber and its mechanical properties and adsorption capacity [J]. Journal of Textile Research, 2020, 41(01): 15-20.
[14] WU Jiao, YU Husheng, WAN Xingyun, TIAN Ping, LI Huimin, HOU Xiaoxin. Preparation and properties of anti-bacterial, anti-mite and anti-mildew functional modified viscose fibers [J]. Journal of Textile Research, 2019, 40(07): 19-23.
[15] FU Chiyu, WANG Cancan, HE Mantang, XIA Zhigang. Contact spinning based on simplified embeddable and locatable system and properties of spun ramie yarn [J]. Journal of Textile Research, 2019, 40(01): 40-45.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 33 -34 .
[2] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 35 -36 .
[3] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 107 .
[4] . [J]. JOURNAL OF TEXTILE RESEARCH, 2003, 24(06): 109 -620 .
[5] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(01): 1 -9 .
[6] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 101 -102 .
[7] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 105 -107 .
[8] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 108 -110 .
[9] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(02): 111 -113 .
[10] . [J]. JOURNAL OF TEXTILE RESEARCH, 2004, 25(03): 7 -8 .
京ICP备14006648号
Copyright 2021 © Editorial office of Journal of Textile Research
Supported by Beijing Magtech Co.Ltd