Journal of Textile Research ›› 2024, Vol. 45 ›› Issue (03): 19-27.doi: 10.13475/j.fzxb.20220900701

• Fiber Materials • Previous Articles     Next Articles

Preparation and performance of copper modified antimicrobial and anti-mite polyamide 6 fiber

ZHENG Xiaodi1, SHENG Pinghou1(), JIANG Jiacen2, LI Rui1, JIAO Hongjuan1, QIU Zhicheng1   

  1. 1. State Key Laboratory of Biobased Fiber Manufacturing Technology, China Textile Academy, Beijing 100025, China
    2. College of Light Industry and Textiles, Inner Mongolia University of Technology, Hohhot, Inner Mongolia 010081, China
  • Received:2022-12-02 Revised:2023-03-12 Online:2024-03-15 Published:2024-04-15
  • Contact: SHENG Pinghou E-mail:382842496@qq.com

Abstract:

Objective The application of copper antimicrobial agent in fiber materials is faced with three major problems. Firstly, the functional nano powder has serious agglomeration and poor compatibility with polymer materials, which makes it difficult to disperse evenly. Secondly, copper is easy to be oxidized and discolored, resulting in poor stability and uniformity of fiber color. Thirdly, spinnability and mechanical properties of fiber decrease with the increase of antimicrobial agent content, therefore it is difficult to increase the content of copper antimicrobial agent in the fiber. It is important to improve the dispersion, interfacial compatibility, and antioxidant properties of copper antimicrobial agent in fibers.

Method In this study, the nano spherical copper antimicrobial agent was coated with oleic acid. Two types of copper modified PA6 antimicrobial masterbatch containing 1.1% and 2.1% copper antimicrobial agent were obtained by squeezing granulation. Copper modified PA6 antimicrobial and anti-mite fibers were obtained by melt spinning and composite spinning, respectively. The structure, morphology and interfacial compatibility of copper antimicrobial agent, thermal stability and spinnability of antimicrobial masterbatch, copper content, mechanical properties, antimicrobial, and anti-mite properties of fiber and fabric samples were analyzed.

Results The diffraction peaks were found sharp with no other impurity peaks appearing, indicating that the sample was well crystallized and was still pure after modification. No obvious weight loss is found during the dehydration at about 100 ℃, which indicated satisfactory hydrophobicity of the sample. Sample C1 showed about 0.4% of weight loss at 300 ℃, and its thermal stability met the requirement of melt spinning, and the dispersion was good without large-size agglomeration under the electron microscope and showed good hydrophobicity with water contact angle of 146°, which was consistent with the TG results. Whether it is melted spinning or composite spinning, pre-oriented yarn sample had high fiber yield of 94%. The fiber yield of draw textured yarn sample is 93% and 94%, respectively. The modified spherical copper antimicrobial agent hardly affected the mechanical properties of PA6, which could be attributed to the reduced agglomeration and improved dispersion of the oleic acid modified spherical copper antimicrobial agent, resulting in fewer large rigid particles in the fiber. The interfacial interaction between PA6 and copper particles was enhanced with the help of oleic acid. The elongation at break of the copper modified PA6 fiber was 29.95% and the tensile breaking strength was 4.43 cN/dtex. For Candida albicans, Staphylococcus aureus and Escherichia coli, copper modified PA6 DTY sample (X1') and copper modified PA6 sheath-core DTY sample (X2') both have high bacteriostasis rate of 99%. The bacteriostasis rate was still over 99% after washing for 50 cycles, indicating that the samples had good resistance to washing and superior long-lasting antibacterial performance. After washing, the copper content of the X1' sample was 1.26% and that of the X2' sample was 1.11%. Compared with the copper content of the two fiber samples before washing, the copper content remained basically the same within the allowable testing error. For mixed test, fungi colony consists of Aspergillus niger, Trichoderma viride, Penicillium funiculosum and Chaetomium globosum, the mildew proof grade of the fiber reached grade 0, meaning no obvious mildew colony under magnifier. X2' samples were woven into fabric for the anti-mite performance test. The result showed that the average number of mites in the test group was 22 and that in control group was 194, suggesting the repellent rate of mites of 89%.

Conclusion The dispersibility of oleic acid coated spherical copper antimicrobial agent and its compatibility with PA6 are good. Copper modified PA6 antimicrobial masterbatch has good thermal stability and spinnability. Copper modified PA6 antimicrobial and anti-mite fiber has high fiber yield of 88% and excellent color consistency at a high antimicrobial addition of 1.1%. The mechanical property of the fiber is adjustable. The antimicrobial, mildewproof and anti-mite properties of fiber samples are strong and durable. Therefore, copper modified PA6 antimicrobial and anti-mite fibers have broad industrial application potentiality in military personal protective equipment, fiber products for medical and health industry and textiles for civil clothing and home decoration.

Key words: spherical copper antimicrobial agent, polyamide 6 fiber, oleic acid, spinnability, antimicrobial property, anti-mite property

CLC Number: 

  • TS102.6

Fig.1

XRD pattern (a) and TG curve (b) of sample C1"

Fig.2

SEM images of samples C0 and C1"

Fig.3

DSC curves (a) and TG curves (b) of samples M0 and M1"

Tab.1

Spinnability of fiber samples"

样品
编号
断裂
强度/
(cN·dtex-1)
断裂
伸长率/
%
POY
制成
率/%
POY-DTY
制成率/
%
DTY总制
成率/
%
X1 3.80 62.28 94
X2 3.45 76.96 94
X1' 4.43 29.95 94 88
X2' 4.36 28.76 93 87

Fig.4

SEM images of fiber sample X1"

Tab.2

EDS scanning results of sample X1"

扫描区域 质量百分比/% 原子百分比/%
C O Cu C O Cu
纤维表面颗粒
点扫描
61.47 28.08 10.46 72.72 24.94 2.34
纤维表面
区域扫描
65.07 34.61 0.32 71.42 28.52 0.07

Fig.5

XRD patterns of fiber samples at equatorial direction (a) and meridian direction (b)"

Tab.3

Comparison of linear density, mechanical properties and orientation factor of fiber samples"

样品
编号
牵伸
倍数
线密度/
dtex
断裂强度/
(cN·dtex-1)
断裂
伸长率/%
取向
因子
X3 1.0 118.91 3.04 86.94 0.57
X4 1.2 100.72 3.34 46.67 0.67
X5 1.3 94.04 3.88 39.67 0.72
X6 1.5 82.22 4.46 21.67 0.74

Fig.6

SEM images of antimicrobial and anti-mite fiber samples after tensile fracture(×5 000).(a)Fracture 1; (b)Fracture 2;(c)Fracture 3;(d)Fracture 4; (e)Fracture 5;(f)Fracture 6"

Tab.4

EDS scanning results of tensile fracture of sample X1"

扫描区域 质量百分比/%
C O Cu Pt K Cl
纤维断裂处
颗粒点扫描
52.67 18.37 -1.79 12.84 9.75 8.15
纤维断裂处
区域扫描
59.44 22.79 -0.51 18.28

Tab.5

Comparison of antimicrobial properties of fiber samples"

样品
编号
洗涤处理 抑菌率%
对大肠杆菌 对金黄色
葡萄球菌
对白色
念珠菌
X1' 未洗涤 >99 >99 >99
洗涤50次 >99 >99 >99
X2' 未洗涤 >99 >99 >99
洗涤50次 >99 >99 >99

Tab.6

Comparison of antimicrobial properties of fabric samples"

样品
编号
洗涤处理 抑菌率/%
对大肠
杆菌
对金黄色
葡萄球菌
对白色
念珠菌

S1
未洗涤 >99 >99 92
洗涤50次 >99 >99 93

S2
未洗涤 >99 >99 >99
洗涤50次 >99 >99 >99

S3
未洗涤 >99 >99 >99
洗涤50次 >99 >99 >99
[1] QIU Q, CHEN S, LI Y, et al. Functional nanofibers embedded into textiles for durable antibacterial properties[J]. Chemical Engineering Journal, 2020. DOI:10.1016/j.cej.2019.123241.
[2] MIKOLAY A, HUGGETT S, TIKANA L, et al. Survival of bacteria on metallic copper surfaces in a hospital trial[J]. Applied Microbiology and Biotechnology, 2010, 87(5): 1875-1879.
doi: 10.1007/s00253-010-2640-1 pmid: 20449737
[3] IBRAHIM N A. Nanomaterials for antibacterial textiles[M]. Pittsburgh: Academic Press, 2015: 191-216.
[4] 王仲霞, 陈春凤. 国内抗菌锦纶6的研发现状[J]. 合成纤维工业, 2021, 44(1):54-58.
WANG Zhongxia, CHEN Chunfeng. Research progress on antibacterial polyamide 6 fiber in China[J]. China Synthetic Fiber Industry, 2021, 44(1): 54-58.
[5] MALACHOVA K, PRAUS P, RYBKOVA Z, et al. Antibacterial and antifungal activities of silver, copper and zinc montmorillonites[J]. Applied Clay Science, 2011, 53(4): 642-645.
doi: 10.1016/j.clay.2011.05.016
[6] 姜兴茂, 刘奇, 郭琳. 二氧化硅包覆银铜纳米颗粒的结构及其抗菌性能[J]. 纺织学报, 2020, 41(11):102-108.
JIANG Xingmao, LIU Qi, GUO Lin. Structure and antibacterial properties of silica coated silver-copper nanoparticles[J]. Journal of Textile Research, 2020, 41(11): 102-108.
[7] JAYASEELAN C, RAHUMAN A A, KIRTHI A V, et al. Novel microbial route to synthesize ZnO nanoparticles using Aeromonas hydrophila and their activity against pathogenic bacteria and fungi[J]. Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy, 2012, 90: 78-84.
doi: 10.1016/j.saa.2012.01.006
[8] SHIVAJI S, MADHU S, SINGH S. Extracellular synthesis of antibacterial silver nanoparticles using psychrophilic bacteria[J]. Process Biochemistry, 2011, 46(9): 1800-1807.
doi: 10.1016/j.procbio.2011.06.008
[9] AMARJARGAL A, TIJING L D, PANT H R, et al. Simultaneous synthesis of TiO2 microrods in situ decorated with Ag nanoparticles and their bactericidal efficiency[J]. Current Applied Physics, 2012, 12(4): 1106-1112.
doi: 10.1016/j.cap.2012.02.003
[10] REN G, HU D, CHENG E, et al. Characterization of copper oxide nanoparticles for antibacterial applications[J]. International Journal of Antibacterial Agents, 2009, 33(6): 587-590.
[11] CAN H, DENG, JI L, et al. Graphene sponge decorated with copper nanoparticles as a novel bactericidal filter for inactivation of Escherichia coli[J]. Chemosphere, 2017, 184:347-357.
doi: 10.1016/j.chemosphere.2017.05.118
[12] UAUY R, OLIVARES M, GONZALEZ M. Essentiality of copper in humans[J]. Nutrition Review, 2010, 45(8): 176-180.
doi: 10.1111/j.1753-4887.1987.tb06081.x
[13] GOPAL A, KANT V, GOPALAKRISHNAN A, et al. Chitosan-based copper nanocomposite accelerates healing in excision wound model in rats[J]. European Journal of Pharmacology, 2014, 731:8-19.
doi: 10.1016/j.ejphar.2014.02.033 pmid: 24632085
[14] LONGANO D, DITARANTO N, CIOFFI N, et al. Analytical characterization of laser-generated copper nanoparticles for antibacterial composite food packaging[J]. Analytical & Bioanalytical Chemistry, 2012, 403: 1179-1186.
[15] DANKOVICH T A, LEVINE J S, POTGIETER N, et al. Inactivation of bacteria from contaminated streams in Limpopo, South Africa by silver-or copper-nanoparticle paper filters[J]. Environmental Science: Water Research & Technology, 2015, 2(1): 85-96.
[16] DASTJERDI R, MONTAZER M. A review on the application of inorganic nano-structured materials in the modification of textiles: focus on anti-microbial properties[J]. Colloids Surf B: Biointerfaces, 2010, 79(1): 5-18.
doi: 10.1016/j.colsurfb.2010.03.029
[17] YUAN G, CRANSTON R. Recent advances in antibacterial treatments of textiles[J]. Overseas Technical Literature Collection, 2008, 60(1): 60-72.
[18] 周能. 油酸包覆Fe3O4/硅橡胶纳米复合材料的制备及其力学与磁性能的研究[D]. 南昌: 南昌大学, 2020: 14-23.
ZHOU Neng. Fabrication of oleic acid-modified Fe3O4/silicone rubber nanocomposites and their mechanical and magnetic properties[D]. Nanchang: Nanchang University, 2020: 14-23.
[19] 李宝兴. 油酸改性氢氧化镁阻燃剂及其在EVA中的应用[D]. 西安: 西安电子科技大学, 2014: 20-42.
LI Baoxing. The surface modification of magnesium hydroxide by oleic acid and its application in EVA[D]. Xi'an: Xidian University, 2014: 20-42.
[20] 郭慧龙, 蔡紫薇, 孙露敏, 等. 不同温度下尼龙6性能和结构变化的原位研究[J]. 高分子学报, 2015(10): 1175-1179.
GUO Huilong, CAI Ziwei, SUN Lumin, et al. Temperature dependent mechanical properties and structure of nylon 6[J]. Acta Polymerica Sinica, 2015(10): 1175-1179.
[21] HOLMES D R, BUNN C W, SMITH D J J. The crystal structure of polyeaproamide: nylon 6[J]. Journal of Polymer Science, 1955, 17: 159-177.
doi: 10.1002/pol.12.v17:84
[22] ARIMOTO H, ISHIBASHI M, HIRAI M, et al. Crystal structure of the γ form of nylon 6[J]. Journal of Polymer Science Part A: General Papers, 1965, 3: 317-326.
doi: 10.1002/pol.10.v3:1
[23] 高称意. 锦纶纤维特性及纤维骨架材料的发展[J]. 中国橡胶, 2004(20): 20-24.
GAO Chenyi. Characteristics of nylon fiber and development of fiber skeleton materials[J]. China Rubber, 2004(20): 20-24.
[24] 王东微. 几种抗菌表面的构建及机理研究[D]. 成都: 西南交通大学, 2016: 8-18.
WANG Dongwei. Preparation of several antibiotic material surfaces and characterization of mechanisms[D]. Chengdu: Southwest Jiaotong University, 2016: 8-18.
[25] 胡晓娟. 铜抗菌作用的生物物理学研究[D]. 上海: 中国科学院研究生院(上海应用物理研究所), 2016: 35-36.
HU Xiaojuan. Biophysical insights into the antibacterial mechanism of copper[D]. Shanghai: Graduate School of Chinese Academy of Sciences (Shanghai Institute of Applied Physics), 2016: 35-36.
[1] WEI Yihui, ZHANG Yujing, DENG Huihua, DENG Qinghui, CHEN Haoqiang, ZHANG Xuzhen, YU Bin, ZHU Feichao. Preparation of high melt flowing index polyethylene masterbatch and spinnability of infrared melt-blown nonwovens [J]. Journal of Textile Research, 2024, 45(02): 28-35.
[2] LIU Ya, ZHAO Chen, ZHUANG Xupin, ZHAO Yixia, CHENG Bowen. Fabrication and properties of metallocene polyethylene spunbond filament based on Polyflow simulation [J]. Journal of Textile Research, 2023, 44(12): 1-9.
[3] LIU Xingchen, QIAN Yongfang, LÜ Lihua, WANG Ying. Fabrication and properties of electrospun nanofibrous membranes from blending collagen peptides/polyethylene glycol [J]. Journal of Textile Research, 2023, 44(08): 34-40.
[4] HU Baoji, ZHANG Qiaoling, WANG Xu. Polyethylene glycol modified thermoplastic epoxy resin and its spinnability [J]. Journal of Textile Research, 2023, 44(02): 63-68.
[5] REN Jiawei, ZHANG Shengming, JI Peng, WANG Chaosheng, WANG Huaping. Preparation and properties of phosphorus-silicon modified flame retardant and anti-dripping polyester fiber [J]. Journal of Textile Research, 2023, 44(02): 1-10.
[6] XIONG Tanping, TAN Fei, HUANG Cheng, YAN Kelu, ZOU Ni, WANG Zheng, YE Jingping, JI Bolin. Antimicrobial properties of chloramine-grafted polyester/polyamide microfiber knitted fabrics [J]. Journal of Textile Research, 2022, 43(08): 101-106.
[7] CHEN Yong, WU Jing, WANG Chaosheng, PAN Xiaohu, LI Naixiang, DAI Junming, WANG Huaping. Preparation and environmental degradation behavior of biodegradable poly (butylene adipate-co-terephthalate) fiber [J]. Journal of Textile Research, 2022, 43(02): 37-43.
[8] YU Meiqiong, YUAN Hongmei, CHEN Lihui. Rheological properties of cellulose/LiCl/ N, N-dimethylacetamide solution [J]. Journal of Textile Research, 2021, 42(05): 23-30.
[9] WANG Ying, WANG Yiting, WU Jiaqing, GUO Yafei, HAO Xinmin. Preparation of compound antistatic spinning oil for bio-based polyamide 56 and its effect on staple fiber spinnability [J]. Journal of Textile Research, 2021, 42(01): 84-89.
[10] QIN Yimin. Clinical applications of silver containing alginate wound dressings [J]. Journal of Textile Research, 2020, 41(09): 183-190.
[11] LIU Yanchun, BAI Gang. Application of berberine in polyacrylonitrile/cellulose acetate composite fiber dyeing [J]. Journal of Textile Research, 2020, 41(05): 94-98.
[12] LIN Jiameng, WAN Ailan, MIAO Xuhong. Preparation and properties of polypyrrole/silver conductive polyester fabrics [J]. Journal of Textile Research, 2020, 41(03): 113-117.
[13] SONG Le, SHEN Lanping, HUANG Xianwen, HENG Fangfang, MA Hongbo, OUYANG Qin, CHEN Peng, WANG Xuan. Preparation and properties of lignin/polyacrylonitrile composite fibers [J]. Journal of Textile Research, 2020, 41(02): 7-12.
[14] GAO Jing, ZHANG Jun, ZHAO Zeyang, LI Wandi, WANG Jiajun, WANG Lu. Antibacterial durability and wearability of polyester/cotton fabric modified collaboratively by graphene oxide and TiO2/SiO2 [J]. Journal of Textile Research, 2019, 40(10): 120-126.
[15] LEI Pengfei, HUANG Yawei, YUAN Senhao, LI Hongyan, WANG Chenglong, ZHENG Jinhuan. In-situ synthesis of calcium carbonate from oleic acid and application there of in wet coating of polyamide [J]. Journal of Textile Research, 2019, 40(05): 70-77.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!