纺织学报 ›› 2022, Vol. 43 ›› Issue (09): 64-69.doi: 10.13475/j.fzxb.20210800506

• 纤维材料 • 上一篇    下一篇

磁场诱导结构生色海藻酸钙纤维的快速制备及其性能

杨春利1,2, 周伟贤2, 梁京龙2, 林桂圳2, 刘杰1,2,3, 倪延朋1,2,3, 刘云1,2,3, 商胜龙1,2,3(), 朱平1,2,3   

  1. 1.青岛大学 功能纺织品与先进材料研究院, 山东 青岛 266071
    2.青岛大学 纺织服装学院, 山东 青岛 266071
    3.青岛大学 省部共建生物多糖纤维成形与生态纺织国家重点实验室, 山东 青岛 266071
  • 收稿日期:2021-08-02 修回日期:2022-05-02 出版日期:2022-09-15 发布日期:2022-09-26
  • 通讯作者: 商胜龙
  • 作者简介:杨春利(1994—),女,硕士生。主要研究方向为智能控温纤维及纺织品。
  • 基金资助:
    国家重点研发计划项目(2020YFC1910305);省部共建生物多糖纤维成形与生态纺织国家重点实验室(青岛大学)开放课题资助项目(TSKT202105)

Rapid preparation and properties of structural colored calcium alginate fibers triggered by magnetic field

YANG Chunli1,2, ZHOU Weixian2, LIANG Jinglong2, LIN Guizhen2, LIU Jie1,2,3, NI Yanpeng1,2,3, LIU Yun1,2,3, SHANG Shenglong1,2,3(), ZHU Ping1,2,3   

  1. 1. Institute of Functional Textiles and Advanced Materials, Qingdao University, Qingdao, Shandong 266071, China
    2. College of Textile & Clothing, Qingdao University, Qingdao, Shandong 266071, China
    3. State Key Laboratory of Bio-Fibers and Eco-Textiles, Qingdao University, Qingdao, Shandong 266071, China
  • Received:2021-08-02 Revised:2022-05-02 Published:2022-09-15 Online:2022-09-26
  • Contact: SHANG Shenglong

RichHTML

18

PDF (PC)

320

摘要：

为制备颜色饱和度高、力学性能优良的结构生色海藻酸钙纤维,首先以溶剂热法制备了磁性微球,然后将其分散至聚乙二醇二丙烯酸酯中,使磁性微球在磁场下自组装,在海藻酸钙纤维表面构筑结构色涂层,分析了影响结构生色海藻酸钙纤维显色性能和力学性能的因素。结果表明:当磁性微球的粒径分别为125、145、190 nm时,其在海藻酸钙纤维表面固化后得到了蓝色、绿色和红色的结构色,磁性微球结构色涂层可对海藻酸钙纤维进行较好地包覆,其主要成分为立方相Fe3O4,可使纤维的断裂强力由纯海藻酸钙纤维的78 cN分别增加到158、162、169 cN,断裂伸长率也得到了显著提高。

关键词: 海藻酸钙纤维, 结构生色, 磁场诱导, 磁性微球, 紫外光固化, 湿法纺丝

Abstract:

To prepare structural colored calcium alginate fibers with high color saturation and satisfactory mechanical properties, magnetic particles were prepared by solvothermal method before dispersing them in the polyethylene glycol diacrylate. A structural color coating was constructed on the surface of calcium alginate fibers by self-assembly of magnetic particles, and factors affecting the color rendering and mechanical properties of the fiber were analyzed. The results show that when the diameters of the magnetic particle are 125, 145 and 190 nm, blue, green and red structural colors were obtained after curing on the surface of calcium alginate fibers, respectively. The coatings of magnetic particles structure color can better achieved on calcium alginate fiber, and the main component is cubic Fe3O4. The mechanical properties of the structural colored calcium alginate fibers have been significantly improved, and the breaking strength has been increased from 78 cN to 158, 162 and 169 cN, respectively, along with the improved elongation at break.

Key words: calcium alginate fiber, structural color, magnetic field triggered, magnetic particle, ultraviolet curing, wet spinning

中图分类号: 

  • TS102.6

图1

结构生色海藻酸钙纤维制备流程图"

图2

不同粒径磁性微球SEM照片和粒径分布图"

图3

平均粒径为190 nm磁性微球的TEM照片和能谱图"

图4

不同粒径磁性微球的PEGDA分散液 在外界磁场作用下的显色情况"

图5

磁性微球的XRD图"

图6

不同粒径磁性微球制备的结构生色海藻酸钙纤维的数码照片和光谱图"

图7

结构色为红色的海藻酸钙纤维的SEM照片"

图8

结构生色海藻酸钙纤维力学性能"

[1] 赵洪. 海藻酸纤维/棉混纺面料整理工艺研究[J]. 纺织导报, 2020 (5): 62-64.
ZHAO Hong. Study on finishing technology of alginate fiber/cotton blended fabric[J]. China Textile Leader, 2020 (5): 62-64.
[2] CI Meiyu, LIU Jie, LIN Li, et al. Preparation and characterization of hydroxypropyl methylcellulose modified alginate fiber[J]. Journal of Physics: Conference Series, 2021. DOI: 10.1088/1742-659611742-6596/179011/012073.
doi: 10.1088/1742-659611742-6596/179011/012073
[3] CHEN Hao, GAO Yang, REN Xiuyan, et al. Alginate fibertoughened gels similar to skin intelligence as ionic sensors[J]. Carbohydrate Polymers, 2020. DOI: 10.1016/j.carbpol.2020.116018.
doi: 10.1016/j.carbpol.2020.116018
[4] ZHANG Miao, ZHAO Xia. Alginate hydrogel dressings for advanced wound management[J]. International Journal of Biological Macromolecules, 2020(162): 1414-1428.
[5] ZOU Xiaolong, SHANG Shenglong, LIU Jie, et al. Facile fabrication of temperature triggered thermochromic core-sheath alginate microfibers from microfluidic spinning[J]. Fibers and Polymers, 2021, 22(6): 1535-1542.
doi: 10.1007/s12221-021-0778-3
[6] LIU Jie, LIU Yun, MIAO Dagang, et al. Gelation modification of alginate nonwoven fabrics[J]. Fibers and Polymers, 2018, 19(8): 1605-1610.
doi: 10.1007/s12221-018-8287-8
[7] LI Zhaoyi, SUN Liang, FU Zhongjun, et al. Coloration of calcium alginate fiber with dye and auxiliary derived from polyvinylamine (PVAm): I: complex dyeing with polymeric dyes containing PVAm[J]. Fibers and Polymers, 2021, 22(3): 720-727.
doi: 10.1007/s12221-021-0213-9
[8] SHI Xiaodi, HE Jialei, XIE Xinhui, et al. Photonic crystals with vivid structure color and robust mechanical strength[J]. Dyes and Pigments, 2019, 165: 137-143.
doi: 10.1016/j.dyepig.2019.02.023
[9] ZENG Qi, DING Chen, LI Qingsong, et al. Rapid fabrication of robust, washable, self-healing superhydrophobic fabrics with non-iridescent structural color by facile spray coating[J]. RSC Advances, 2017(7): 8443-8452.
[10] LIU Guojin, ZHOU Lan, WU Yujiang, et al. Optical properties of three-dimensional P(St-MAA) photonic crystals on polyester fabrics[J]. Optical Materials, 2015(42): 72-79.
[11] LIU Guojin, ZHOU Lan, ZHANG Guoqing, et al. Fabrication of patterned photonic crystals with brilliant structural colors on fabric substrates using ink-jet printing technology[J]. Materials & Design, 2017(114): 10-17.
[12] LI Qingsong, ZHANG Yafeng, SHI Lei, et al. Additive mixing and conformal coating of noniridescent structural colors with robust mechanical properties fabricated by atomization deposition[J]. ACS Nano, 2018(12): 3095-3102.
[13] LIU Guojin, HAN Pengshuai, WU Yu, et al. The preparation of monodisperse P(St-BA-MAA)@disperse dye microspheres and fabrication of patterned photonic crystals with brilliant structural colors on white substrates[J]. Optical Materials, 2019. DOI: 10.1016/j.optmat.2019.109503.
doi: 10.1016/j.optmat.2019.109503
[14] LI Yichen, FAN Qingsong, WANG Xiaohui, et al. Shear-induced assembly of liquid colloidal crystals for large-scale structural coloration of textiles[J]. Advanced Functional Materials, 2021. DOI: 10.1002/adfm.20.2010746.
doi: 10.1002/adfm.20.2010746
[15] WANG Xiaohui, LI Yichen, ZHAO Qian, et al. High structural stability of photonic crystals on textile substrates, prepared via a surface-supported curing strategy[J]. ACS Appllied Materials & Interfaces, 2021, 13: 19221-19229.
[16] SHANG Shenglong, ZHANG Qinghong, WANG Hongzhi, et al. Fabrication of magnetic field induced structural colored films with tunable colors and its application on security materials[J]. Journal of Colloid and Interface Science, 2017 (485): 18-24.
[17] LIU Zhifu, ZHANG Qinghong, WANG Hongzhi, et al. Magnetic field induced formation of visually structural colored fiber in micro-space[J]. Journal of Colloid and Interface Science, 2013 (406): 18-23.
[18] CALDERON F L, STORA T, MONVAL O M, et al. Direct measurement of colloidal forces[J]. Physical Review Letters, 1994, 72(18): 2959-2962.
doi: 10.1103/PhysRevLett.72.2959
[19] WANG Hui, CHEN Qianwang, YU Yifei, et al. Size-and solvent-dependent magnetically responsive optical diffraction of carbon-encapsulated superparamagnetic colloidal photonic crystals[J]. The Journal of Physical Chemistry C, 2011(115): 11427-11434.
[1] 杜璇, 丁长坤, 岳程飞, 苏杰梁, 闫旭焕, 程博闻. 凝固浴对再生胶原纤维结构与性能的影响[J]. 纺织学报, 2022, 43(09): 58-63.
[2] 薛超, 朱浩, 杨晓川, 任煜, 刘婉婉. 聚氨酯基碳纳米管-液态金属导电纤维的制备及其性能[J]. 纺织学报, 2022, 43(07): 29-35.
[3] 戚栋明, 樊高晴, 虞一浩, 符晔, 张艳, 陈智杰. 蓖麻油基紫外光固化水性涂料墨水制备及其印花性能[J]. 纺织学报, 2022, 43(05): 26-31.
[4] 朱小威, 韦天琛, 李亦江, 邢铁玲, 陈国强. 聚苯乙烯/铁-单宁酸配合物微球在棉织物上的结构生色[J]. 纺织学报, 2022, 43(05): 32-37.
[5] 陈子晗, 姚勇波, 生俊露, 颜志勇, 张玉梅, 王华平. 纤维素/海藻酸钙共混纤维的制备及其性能[J]. 纺织学报, 2021, 42(12): 15-20.
[6] 王晓辉, 刘国金, 邵建中. 纺织品仿生结构生色[J]. 纺织学报, 2021, 42(12): 1-14.
[7] 陈纤, 李猛猛, 赵昕, 董杰, 滕翠青. 纳米芳纶气凝胶纤维的制备与微观结构调控[J]. 纺织学报, 2021, 42(11): 17-23.
[8] 何聚, 刘晓辉, 苏晓伟, 林生根, 任元林. 星型无卤阻燃剂改性粘胶纤维的制备及其性能[J]. 纺织学报, 2021, 42(10): 34-40.
[9] 朱小威, 韦天琛, 邢铁玲, 陈国强. 非晶光子晶体结构色织物的制备及其数值模拟[J]. 纺织学报, 2021, 42(09): 90-96.
[10] 徐凯, 田星, 曹英, 何雅琦, 夏延致, 全凤玉. 阻燃涤纶/海藻酸钙纤维复合材料的制备及其性能[J]. 纺织学报, 2021, 42(07): 19-24.
[11] 王慧云, 王萍, 李媛媛, 张岩. 中空多孔异形聚丙烯腈纤维的制备及其性能[J]. 纺织学报, 2021, 42(03): 50-55.
[12] 刘明雪, 赵倩, 王晓辉, 刘琼溪, 邵建中. 磁控溅射纳米膜与不同纺织基材的结合牢度[J]. 纺织学报, 2021, 42(02): 135-141.
[13] 王晓辉, 李义臣, 刘国金, 唐族平, 周岚, 邵建中. 柔性光子晶体结构生色膜的制备及其光学性质[J]. 纺织学报, 2021, 42(02): 12-20.
[14] 马跃, 郭静, 殷聚辉, 赵秒, 宫玉梅. 纤维素/氧化纤维素/南极磷虾蛋白复合抗菌纤维的制备与表征[J]. 纺织学报, 2020, 41(11): 34-40.
[15] 庞雅莉, 孟佳意, 李昕, 张群, 陈彦锟. 石墨烯纤维的湿法纺丝制备及其性能[J]. 纺织学报, 2020, 41(09): 1-7.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
京ICP备14006648号　 京公网安备11010502044800号
版权所有 © 2021 《纺织学报》编辑部
地址： 北京市朝阳区延静里中街3号主楼6层《纺织学报》杂志社　邮政编码：100025　
电话：010-65017711,65917740　传真：010-65016539　Email:fangzhixuebao@vip.126.com
本系统由北京玛格泰克科技发展有限公司设计开发